一种生物质炭负载磁性物质复合吸附材料及其制备方法、应用方法技术
Biomass carbon bearing magnetic material composite adsorption material, preparation method and application method thereof
The invention discloses a biomass carbon supported magnetic material composite adsorption material, a preparation method and an application method thereof, belonging to the field of water treatment. The invention of biomass with cobalt salt and nickel salt mixed grinding, obtain mixture, then the mixture under the protection of inert gas, and then cooling, namely calcination, magnetic material composite adsorption material load of biomass carbon. Plan the preparation required fewer steps, friendly to the environment, can be prepared by the invention of biomass carbon prepared by the method of load magnetic material composite adsorption material has good adsorption effect, preparation method of the invention has good prospects for industrial production.
【技术实现步骤摘要】
一种生物质炭负载磁性物质复合吸附材料及其制备方法、应用方法，属于生物质废弃物综合利用研究领域。
技术介绍
纺织、造纸、化妆品等行业排放的染料大多数具有毒性且降低了水体的透光率，对水体造成了严重污染。活性炭吸附是将染料从废水中去除的主要手段，但活性炭较高的制备成本使其应用受到一定的限制。在广大农村里，每年产生大量的麦秸、稻草、玉米秆、甘蔗渣等农业生物质，这些生物质中含有丰富的羟基、醛基、醚基、羧基等极性基团很容易与染料分子相互作用而吸附染料分子。农业生物质作为吸附剂的最大优点是经济，费用一般不到活性炭的10％，但该类吸附剂的直接吸附效果并不理想，需要进行相应的改性处理。磁性纳米材料作为一种新型的吸附剂，其快速、高效、便捷、可回收等特性为污水处理开辟了新的方向和思路。与传统的吸附剂相比，磁性吸附剂可以避免使用过滤，离心方法，从而实现利用较少的能量来达到小尺寸吸附剂从溶液中的分离的目的。虽然磁性材料在染料废水处理方面具有诸多优势，复杂的制备步骤和高昂的制造成本使其并未得到大规模的应用。申请公布号为CN103949212A的中国专利技术专利(申请公布日为2014年07月...
【技术保护点】
一种生物质炭负载磁性物质复合吸附材料的制备方法，其特征在于，所述制备方法包括以下步骤：1)将生物质与钴盐和镍盐混合后研磨均匀，得到混合物；2)将步骤1)中所得的混合物在惰性气体保护下，在600～1000℃煅烧1～3h，然后冷却，即得生物质炭负载磁性物质复合吸附材料。
【技术特征摘要】
1.一种生物质炭负载磁性物质复合吸附材料的制备方法，其特征在于，所述制备方法包括以下步骤：1)将生物质与钴盐和镍盐混合后研磨均匀，得到混合物；2)将步骤1)中所得的混合物在惰性气体保护下，在600～1000℃煅烧1～3h，然后冷却，即得生物质炭负载磁性物质复合吸附材料。2.如权利要求1所述的生物质炭负载磁性物质复合吸附材料的制备方法，其特征在于，步骤1)中所述生物质为甘蔗粉，所述甘蔗粉的制备方法包括以下步骤：除去甘蔗中的汁水得甘蔗渣，将甘蔗渣干燥，然后粉碎，得甘蔗粉。3.如权利要求1所述的生物质炭负载磁性物质复合吸附材料的制备方法，其特征在于，所述钴盐和镍盐分别为六水合氯化钴和六水合氯化镍。4.如权利要求3所述...
【专利技术属性】
技术研发人员：胡鹏，牛静，柳准，刘卉，赵梦溪，刘景民，
申请(专利权)人：黄淮学院，河南省华鼎高分子合成树脂有限公司，
类型：发明
国别省市：河南;41