The invention relates to a method for preparing micro-nano silver particles in an aqueous solution system, which comprises the following steps: mixing silver saline solution with aqueous solution of complexing agent to prepare silver complex precursor solution, then dropping and mixing with aqueous solution of reducing agent at the same time, carrying out one-step reduction reaction to obtain micro-nano silver particles. The invention reacts in aqueous solution under normal temperature and pressure, does not use macromolecule polymer as protective agent and dispersant, and uses hydrazine hydrate as reducing agent to reduce the complex precursor of silver. The preparation method is simple and avoids the residue of polymer on the surface of silver powder. The flower-like micro-and nano-silver particles prepared have regular morphology, uniform particle size distribution, good dispersion, controllable size and high yield.
【技术实现步骤摘要】
水溶液体系中制备微纳米银颗粒的方法
本专利技术公开了水溶液体系中制备微纳米银颗粒的方法，属于微纳米材料银的制备领域。
技术介绍
银微纳米材料具有独特的物理化学性质，在电学、催化、磁学和SERS光谱等领域有着广泛的应用前景。银的微纳米材料的性质与性状、尺寸及结构等因素密切相关。近年来，纳米微粒和纳米材料已成为材料科学领域的研究的热点之一。我国微纳米银的研究和开发起于60年代初，八、九十年代进入快速发展阶段，在这段时期政府投入大，有许多单位参与了银粉制备技术的研究，并生产出许多系列的银粉，填补了国内空白。在我国，生产银粉的厂家虽不少，品种全、质量好的单位不多。跟世界发达国家相比，目前我国生产的银粉品种和系列还不是很全，性能跟国外也还存在一定差距。为了满足多种多样的实际需求，许多研究机构与研究小组也是利用各种方法成功合成出具有不同形状、尺寸和结构的微纳米结构的银材料。形貌控制是一条调控金属纳米结构物理和化学性质的有效途径，因此银的形貌可控制备仍然是现阶段研究的一个焦点。理论计算和实验结果都表明，银纳米颗粒的表面等离子体共振和表面增强拉曼散射性质都高度依赖于它们的形貌。微...
【技术保护点】
1.水溶液体系中制备微纳米银颗粒的方法，包括步骤如下：将银盐水溶液与络合剂水溶液混合制得银的络合物前驱体溶液，然后与还原剂水溶液同时滴加混合，进行一步还原反应，得到微纳米银颗粒。
【技术特征摘要】
1.水溶液体系中制备微纳米银颗粒的方法，包括步骤如下：将银盐水溶液与络合剂水溶液混合制得银的络合物前驱体溶液，然后与还原剂水溶液同时滴加混合，进行一步还原反应，得到微纳米银颗粒。2.根据权利要求1所述的水溶液体系中制备微纳米银颗粒的方法，其特征在于，所述的银盐为硝酸银、乙酸银、硫酸银。3.根据权利要求1所述的水溶液体系中制备微纳米银颗粒的方法，其特征在于，银盐水溶液的浓度为0.01-8g/mL，优选为0.05-1g/mL。4.根据权利要求1所述的水溶液体系中制备微纳米银颗粒的方法，其特征在于，所述的络合剂为柠檬酸、柠檬酸三钠、乙二胺四乙酸或乙二胺四乙酸二钠。5.根据权利要求1所述的水溶液体系中制备微纳米银颗粒的方法，其特征在于，络合剂水溶液的浓度为0.02-0.2g/mL。6.根...
【专利技术属性】
技术研发人员：陈代荣，田尚玲，焦秀玲，
申请(专利权)人：山东大学，
类型：发明