The present invention discloses an 800 MPa cluster strengthened steel sheet. Its chemical composition includes 0.01-0.1% C, 0.5-2% Mn, 0.1-0.6% Si, 0.01-0.1% ALS, 0.01-0.1% Nb, 0.01-0.1% Ti, residual Fe and unavoidable impurities by weight percentage. By controlling the composition and weight percentage and combining high temperature coiling, the nano-sized cluster precipitates with fine size, uniform distribution and high density can be obtained, the strength of ferrite can be significantly strengthened, the strength difference between the two matrix structures (ferrite and martensite) can be reduced, and the high pore expanding performance can be obtained to meet the requirements of users for high strength and high plasticity.
【技术实现步骤摘要】
800MPa级簇团强化型钢板及制备方法
本专利技术涉及高强热轧钢
，具体涉及一种800MPa级簇团强化型钢板及制备方法。
技术介绍
受到环保和节能的影响，钢铁工业需要开发具有节能、节材和优异性能的超高强钢以实现可持续发展。超高强度钢除了要求高的抗拉强度外，还要求具有一定塑韧性、尽可能小的缺口敏感性、高的疲劳强度、良好的工艺性能等。随着纳米科技的发展，纳米材料在力学性能方面展现出高强度、高硬度和高韧性等独特的优势。为了节约资源、降低成本，减少甚至避免昂贵合金元素的使用，降低合金元素含量是设计新型超高强度钢需要注意的问题，同时选用韧性良好、生产工艺简单的铁素体组织为基体，可以克服马氏体钢的快冷要求对材料尺寸的限制，节约能源、简化工艺。纳米析出强化是金属材料最有前途的强韧化机制之一，也是新型超高强度钢最重要的强化机制。综合利用传统的强化机制：细晶强化、固溶强化和位错强化可以获得组织性能的最好匹配。中国专利技术专利申请(公开号CN108004475A、公开日2018.5.8)，为获得优异的强度、塑性和韧性匹配，钢的化学成分重量百分比为：0.10％≤C≤0.20％，1...
【技术保护点】
1.一种800MPa级簇团强化型钢板，其特征在于：化学成分按重量百分比包括：0.01～0.1％的C、0.5～2％的Mn、0.1～0.6％的Si、0.01～0.1％的Als、0.01～0.1％的Nb、0.01～0.1％的Ti，余量为Fe及不可避免的杂质。
【技术特征摘要】
1.一种800MPa级簇团强化型钢板，其特征在于：化学成分按重量百分比包括：0.01～0.1％的C、0.5～2％的Mn、0.1～0.6％的Si、0.01～0.1％的Als、0.01～0.1％的Nb、0.01～0.1％的Ti，余量为Fe及不可避免的杂质。2.根据权利要求1所述800MPa级簇团强化型钢板，其特征在于：所述C的重量百分比为0.065～0.1％。3.根据权利要求1所述800MPa级簇团强化型钢板，其特征在于：所述Mn的重量百分比为0.5～1.55％。4.根据权利要求1所述800MPa级簇团强化型钢板，其特征在于：所述Si的重量百分比为0.1～0.5％。5.根据权利要求1所述800MPa级簇团强化型钢板，其特征在于：所述Als的重量百分比为0.04～0.1％。6.根据权利要求1所述800MPa级簇团强化型钢板，其特征在于：所述Nb的重量百分比为0.04～0.1％。7.根...
【专利技术属性】
技术研发人员：方芳，潘立波，尹云洋，胡俊，陈一鸣，孙伟华，杜小峰，
申请(专利权)人：武汉钢铁有限公司，
类型：发明
国别省市：湖北,42