The manufacturing process of Ag-SnO_2 aggravated rare earth contact materials includes the following steps: (1) firstly, Ag and SnO_2 are added into GeO_2, Gd_2O_3, Sm_2O_3 and YO_3; (2) mixing the above materials; (3) alloying the materials; (4) diffusion annealing; (5) gas pressure is 60 MPa to 80 MPa. Between isostatic forming; 6) sintering; 7) pre-extrusion between 90 MPa and 120 MPa in gas pressure; 8) secondary sintering; 9) extrusion processing, 10) wire or strip processing. The invention has the following beneficial effects: the addition of heavy rare earth optimizes the high temperature stability of the material, makes the contacts high conductivity and high thermal conductivity, thereby enabling them to have good arc erosion resistance.
【技术实现步骤摘要】
银氧化锡加重稀土触头材料的制造工艺
本专利技术属于触头材料领域，具体涉及AgSnO2加重稀土触头材料的制造工艺。
技术介绍
电触头是各种高低压电器的核心部件，广泛应用在航空、航天、航海领域及民用工业的各种交直流接触器、断路器、继电器转换开关中。其性能直接影响整个电器的通断容量，使用寿命和运行可靠性等。电触头材料种类繁多。常用的主要有银基合金和铜基合金，其中银基合金电触头材料大量应用于中小负荷（小于50A）或弱电条件下（小于1A）的低压电器，汽车电器和家用电器中。特别是继电器和接触器这些量大面广的电器，几乎全部采用Ag基触头材料。在银基触头材料中，AgCdO由于具有良好的耐电弧磨损性，抗熔焊性，导电性和导热性，且接触电阻小而稳定性高，被称为“万能触头材料”。但由于AgCdO触头材料在生产、使用和回收过程中存在着“镉毒”的危害，对人体和自然环境具有较大的危害和污染。为此国际电工组织于2003年2月发布《关于在电子电气设备中禁止使用某些有害物质指令》。该指令2006年7月1日起生效。因此，研制和开发新型具有环保功效和良好电接触性能的触头材料成为该领域的热门课题。AgSn...
【技术保护点】
1.银氧化锡加重稀土触头材料的制造工艺，其特征在于，包括以下步骤，步骤1）首先配置材料Ag、SnO2，添加入GeO2、Gd2O3、Sm2O3和Y2O3中的一种或多种；2）上述材料混合3小时；3）进行合金化处理4小时；4）在温度为450度进行扩散退火3小时；5）在气体压力为60MPa~80MPa之间等静化成型；6）在温度为800‑900度之间，进行一次烧结3小时；7）在气体压力为90MPa~120MPa之间进行预挤压加工；8）在温度为800‑900度之间进行二次烧结3小时；9）在温度为800‑900度之间进行挤压3小时，10）线材或带材加工。
【技术特征摘要】
1.银氧化锡加重稀土触头材料的制造工艺，其特征在于，包括以下步骤，步骤1）首先配置材料Ag、SnO2，添加入GeO2、Gd2O3、Sm2O3和Y2O3中的一种或多种；2）上述材料混合3小时；3）进行合金化处理4小时；4）在温度为450度进行扩散退火3小时；5）在气体压力为60MPa~80MPa之间等静化成型；6）在温度为800-900度之间，进行一次烧结3小时；7）在气体压力为90MPa~120MPa之间进行预挤压加工；8）在温度为800-900...
【专利技术属性】
技术研发人员：薛明路，陈凯炼，陈夏，
申请(专利权)人：宁波科扬贵金属合金科技有限公司，
类型：发明
国别省市：浙江,33
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。