The invention provides a halogen-free flame-retardant silicone sealant, which comprises the following raw materials: 80-120 parts of silicone rubber; 5-15 parts of vinyl tributyl ketone oxime silane; 5-15 parts of methyl tributyl ketone oxime silane; 50-80 parts of solid filler; FA_805-10 parts of aluminium hydroxide; 2-5 parts of flame retardant; 1-5 parts of decabromodiphenyl ether; A11001-5 copies of combination agent and 1-3 copies of di-phase tin dilaurate. The sealant provided by the invention can effectively improve the flame retardant performance of the sealant by guaranteeing the original anti-ultraviolet ray ability, anti-displacement ability and elastic recovery ability, and can be used for the curtain wall required for fire protection.
【技术实现步骤摘要】
一种无卤阻燃硅酮耐厚密封胶
本专利技术涉及建筑材料
，具体涉及一种无卤阻燃硅酮耐厚密封胶。
技术介绍
硅酮密封胶由于具有良好的抗紫外线能力，抗位移能力、弹性恢复能力和对常用幕墙材料极佳的粘附性，成为建筑幕墙首选的密封材料之一。硅铜密封胶自身阻燃性不佳，即使加入超细二氧化硅、碳酸钙等填料，接触火焰后一经点燃还是会持续燃烧。随着世界各国对建筑防火级别要求的提高及对幕墙防火性能的关注，硅酮耐候密封胶的阻燃性能改进已成为必然。因此，针对上述问题，本专利技术提出了一种新的技术方案。
技术实现思路
本专利技术的目的是提供一种具有优异的阻燃性能的无卤阻燃硅酮耐厚密封胶。本专利技术是通过以下技术方案来实现的：一种无卤阻燃硅酮耐厚密封胶，包括以下重量份数的原料组成：硅橡胶80~120份；乙烯基三丁酮肟基硅烷5~15份；甲基三丁酮肟基硅烷5~15份；固体填料50~80份；氢氧化铝FA-805~10份；阻燃剂2~5份；十溴二苯醚1~5份；偶联剂A11001~5份；二月桂酸二相基锡1~3份。优选地，所述固体填料包括以下重量份原料组成：气相法白炭黑15~30份；纳米活性碳酸钙20~30份；石墨粉15~30份。优选地，所述阻燃剂为氮系磷系复配阻燃剂。优选地，其制备方法为将硅橡胶、乙烯基三丁酮肟基硅烷、甲基三丁酮肟基硅烷、固体填料、氢氧化铝FA-80、阻燃剂、十溴二苯醚、偶联剂A1100和二月桂酸二相基锡将比例加入到捏合机中，加热抽真空脱水制得基料。本专利技术的有益效果是：本专利技术提出的密封胶在保证原有的抗紫外线能力，抗位移能力、弹性恢复能力，有效地提高了其阻燃性能，可用于防火要求...
【技术保护点】
1.一种无卤阻燃硅酮耐厚密封胶，其特征在于：包括以下重量份数的原料组成：硅橡胶 80~120份；乙烯基三丁酮肟基硅烷 5~15份；甲基三丁酮肟基硅烷 5~15份；固体填料 50~80份；氢氧化铝FA‑80 5~10份；阻燃剂 2~5份；十溴二苯醚 1~5份；偶联剂A1100 1~5份；二月桂酸二相基锡 1~3份。
【技术特征摘要】
1.一种无卤阻燃硅酮耐厚密封胶，其特征在于：包括以下重量份数的原料组成：硅橡胶80~120份；乙烯基三丁酮肟基硅烷5~15份；甲基三丁酮肟基硅烷5~15份；固体填料50~80份；氢氧化铝FA-805~10份；阻燃剂2~5份；十溴二苯醚1~5份；偶联剂A11001~5份；二月桂酸二相基锡1~3份。2.根据权利要求1所述一种无卤阻燃硅酮耐厚密封胶，其特征在于：所述固体填料包括以下重量份原料组成：气相法白炭黑1...