The invention belongs to the technical field of nano-material preparation, and relates to a fluorinated nano-diamond material, a preparation method and its application in the field of thermal catalysis. The method uses nano-diamond, perfluorinated iodobutane as raw materials and fluorinates under xenon light for several hours to form fluorine-doped nano-diamond (0.3 wt% of fluorine doping is the optimal ratio), and then applies to the oxidation dehydrogenation of ethylbenzene to styrene, showing excellent thermal catalytic performance. The preparation method provided by the invention is safe, environmentally friendly, mild and controllable, and simple in process. The obtained fluorinated nanodiamond has stable physical and chemical properties and good thermal catalytic performance, which has a broader application in other industrial catalytic fields.
【技术实现步骤摘要】
一种氟化纳米金刚石材料及其制备方法和应用
本专利技术属于纳米材料制备
，涉及一种氟化纳米金刚石材料及其制备方法和其在热催化领域的应用。
技术介绍
苯乙烯（styrene,ST）是工业上一种重要的单体，广泛用于聚合物、共聚物、生产塑料以及合成橡胶的原料。如橡胶改性抗冲击聚苯乙烯、丙烯腈-丁二烯-苯乙烯三聚体（ABS）、苯乙烯-丙烯腈共聚体（SAN）和丁苯橡胶（SBR）等等（ChemSusChem2016,9,662-666;ACSCatal.2015,5,6426-6435;）。工业上制备苯乙烯的方法主要是在催化剂的帮助下，乙苯直接热催化脱氢（DH）制得苯乙烯（Appl.Catal.A:Gen.1994,112,117-124;Appl.Catal.A:Gen.1995,133,219-239;Chem.Commun.2014,50,7810-7812;Angew.Chem.Int.Ed.2010,49,8640-8644）。然而该方法乙苯转化率低（＜50%），需要的反应温度较高（＞600℃），并且在动力学上属于吸热反应（ΔHο=+117.6kJ·mol-1）...
【技术保护点】
1.一种氟化纳米金刚石材料的制备方法，其特征在于：包括以下步骤：1) 将纳米金刚石粉末加入带有磁子的圆底烧瓶，并加入全氟碘代丁烷液体，使其混合均匀；2) 将步骤1) 所得的混合样置于水浴30℃恒温体系中搅拌，并在氙灯下光照1~5小时，使纳米金刚石能够氟化完全；3) 将步骤2) 得到的混合样离心，洗涤，并在80℃烘箱中过夜烘干，即得氟化纳米金刚石材料。
【技术特征摘要】
1.一种氟化纳米金刚石材料的制备方法，其特征在于：包括以下步骤：1)将纳米金刚石粉末加入带有磁子的圆底烧瓶，并加入全氟碘代丁烷液体，使其混合均匀；2)将步骤1)所得的混合样置于水浴30℃恒温体系中搅拌，并在氙灯下光照1~5小时，使纳米金刚石能够氟化完全；3)将步骤2)得到的混合样离心，洗涤，并在80℃烘箱中过夜烘干，即得氟化纳米金刚石材料。2.根据权利要求1所述的一种氟化纳米金刚石材料的制备方法，其特征在于：步骤1)中，所述纳米金刚石用量为40~80mg，全氟碘代丁烷...