A preparation method of graphene-based composite conductive film with excellent conductivity is introduced. Firstly, the filter paper is used as the raw material of the fiber, and the slurry containing cellulose fiber, graphene oxide and silver ammonia complex (Ag(NH3)2OH) is prepared by the high-speed rotation of the cooker rotor. Then, the slurry is heated and reduced by graphene oxide itself. The silver-ammonia complex was reduced to silver nanoparticles, and the complex of graphene oxide, silver nanoparticles and cellulose fibers was induced. Cellulose/graphene oxide/silver nanoparticle composite film was formed after the product was filtered and dewatered in a sufficiently water-washed filter. Then graphene oxide was reduced to graphene by hydrazine vapor as a reducing agent, and cellulose/graphene/silver nanoparticle flexible thin films with excellent conductivity and electrochemical properties were obtained. Membrane.
【技术实现步骤摘要】
一种导电性能优异的石墨烯基复合导电薄膜的制备方法
本专利技术涉及一种柔性石墨烯导电复合薄膜的制备方法。
技术介绍
市场对新一代柔性便携的电子产品如可穿戴设备、可卷曲显示器、可折叠智能手机、可植入医疗芯片、电子皮肤等有着迫切的需求与期待,当前的供能和储能电子设备显得过沉、过厚、过大,已经难以满足这一新兴领域的要求,是故,发展轻薄便携的高性能柔性储能体系势在必行。在现有的各种储能体系中,全固态柔性超级电容器因其快的充放电速度、高的功率密度、宽的工作温度、好的稳定性、长的使用寿命以及出色的安全性而备受关注,尤其是石墨烯基全固态柔性超级电容器近年来发展迅猛,具有良好的发展空间和应用前景。遗憾的是,当前所开发的绝大多数全固态柔性超级电容器的储能特性依然难以令人满意,比如比电容依然较小、能量密度仍旧不高,倍率性能也相对较差。为此,如何通过简单经济的方法宏量制备具有良好导电性的自支持柔性薄膜,进而构筑出具有优异电化学行为的全固态柔性超级电容器成为了目前超级电容器领域的难点问题和重点所在。
技术实现思路
本专利技术目的在于提供一种导电性优异的自支持柔性石墨烯基导电复合薄膜的制备方法。本专利技术目的是通过以下技术方案实现的:一种石墨烯基导电复合薄膜的制备方法,首先以滤纸作为纤维原料,借助料理机转子的高速旋转制备含有纤维素纤维、氧化石墨烯和银氨络合物(Ag(NH3)2OH)的混合浆料,尔后加热处理,利用氧化石墨烯本身的还原性将银氨络合物还原成银纳米颗粒,同时诱发氧化石墨烯、银纳米颗粒、纤维素纤维三者的复合。产物经抽滤装置抽滤脱水并充分水洗后形成纤维素/氧化石墨烯/银纳米颗粒复合薄 ...
【技术保护点】
1.一种石墨烯基导电复合薄膜的制备方法,其特征在于,按以下步骤: (1) 将滤纸剪成碎片后与氧化石墨烯水分散液一起加至料理机中,利用料理机转子的高速旋转将滤纸打碎,制成纤维素纤维+氧化石墨烯浆料;所述石墨烯:纤维素纤维的质量比5:95‑70:30;(2) 将步骤(1)的混合浆料转移至烧杯中,在快速磁力搅拌下加入过量的浓度为0.1‑0.5M的银氨溶液,然后升温至70‑90 oC并反应20‑40 min;(3) 将步骤(2)的产物在漏斗中抽滤脱水,于抽滤装置滤膜表面形成纤维素/氧化石墨烯/银纳米颗粒复合薄膜;加水反复洗涤干净后,将其在湿润状态下从滤膜表面缓缓地整体撕下,并转移至反应釜中,悬空放置;接着在反应釜内衬底部加入水合肼,密封好后置于80‑110oC的烘箱中保持8‑24 h,利用肼蒸气将其中的氧化石墨烯彻底还原成石墨烯制得纤维素/石墨烯/银纳米颗粒复合薄膜;所述水合肼与纤维素/氧化石墨烯/银纳米颗粒复合薄膜的质量比为1:1.5‑2.5;所述制得的纤维素纤维/石墨烯/银纳米颗粒复合薄膜表面层结构为银纳米颗粒相互堆叠形成的连续银纳米颗粒膜,内部为纤维素‑石墨烯‑银纳米颗粒的成分、且纤维素 ...
【技术特征摘要】
1.一种石墨烯基导电复合薄膜的制备方法,其特征在于,按以下步骤:(1)将滤纸剪成碎片后与氧化石墨烯水分散液一起加至料理机中,利用料理机转子的高速旋转将滤纸打碎,制成纤维素纤维+氧化石墨烯浆料;所述石墨烯:纤维素纤维的质量比5:95-70:30;(2)将步骤(1)的混合浆料转移至烧杯中,在快速磁力搅拌下加入过量的浓度为0.1-0.5M的银氨溶液,然后升温至70-90oC并反应20-40min;(3)将步骤(2)的产物在漏斗中抽滤脱水,于抽滤装置滤膜表面形成纤维素/氧化石墨烯/银纳米颗粒复合薄膜;加水反复洗涤干净后,将其在湿润状态下从滤膜表面缓缓地整体撕下,并转移至反应釜中,悬空放置;接着在反应釜内衬底部加入水合肼,密封好后置于80-110oC的烘箱中保持8-24h,利用肼蒸气将其中的氧化石墨烯彻底还原成石墨烯制得纤维素/石墨烯/银纳米颗粒复合薄膜;所述水合肼与纤维素/氧化石墨烯/银纳米颗粒复...