The invention discloses a superfine powder of alkali slag cement, which is made of 98 99% alkali slag discharged from industrial lime alkali production by salt chemical industry and 1 2% chlorine remover by mixing and stirring, solidifying and drying at 100 degrees, and grinding to produce superfine powder of cement with specific surface area greater than 400 500_/kg, which can replace 40% of cement products. It can advance the setting time of cement by 20 to 40 minutes, increase the hydration strength of cement by 8 to 12 mpa, increase the specific surface area by 100 to 150_/kg, reduce the water consumption of cement by 15 to 30%, increase the wear resistance of cement by 10 to 15 times, increase the compatibility of cement products by 100 mm and improve the compatibility of cement products. The output of cement is 20 to 30 tons per hour, which directly reduces the cost of cement by 80 yuan per ton. It also protects the environment from secondary pollution.
【技术实现步骤摘要】
一种碱渣水泥超细粉及其制备方法
本专利技术属于环保水泥生产
，具体涉及的是用工业废渣碱渣制备的一种水泥超细粉。
技术介绍
随着我国经济改革开放的不断发展，特别是盐化工行业新技术更加突飞猛进，造成大量的天然矿产资源石灰石等消耗，也造成对环境污染压力的问题日益突出，生产的工业石碱后排出大量的废渣比较难以处理，只能堆放填埋，导致二次污染地下水资源，碱渣中含有大量的氧化钙、氯化钙等成分，含水量在50%左右，为了变废为宝，我们将工业废渣碱渣，经特定工艺生产一种超细粉，用于替代水泥产品，为减轻水泥行业大量消耗天然资源石灰石、粘土，煤碳等材料，减轻了水泥行业对大气污染的问题，同时节约了资源和能源，又大量消耗了盐化工行业的工业废渣碱渣，也节约了水泥企业的生产成本。
技术实现思路
专利技术的目的：本专利技术的目的是为了解决大量的盐化工废渣碱渣堆放和填埋，严重污染地下水资源等问题，提供一种生产成本低，产品性能好的水泥超组粉及其制备方法。技术方案：本专利技术所述的水泥超细粉及其制备方法，按质量百分比计为，由98-99%碱渣，辅以1-2%的除氯剂为100%为原材料，经混合搅拌成型和烘干...
【技术保护点】
1.一种碱渣水泥超细粉，其特征在于，按质量百分比计为，盐化工生产工业石碱后排出的废渣碱渣98‑99%，辅以除氯剂1‑2%为100%为原材料，经混合搅拌均匀，制成微型细颗粒1‑2mm，堆放固化，送入烘干窑经100摄氏度烘干脱除自由水和结晶水，即得水泥超细粉产品。
【技术特征摘要】
1.一种碱渣水泥超细粉，其特征在于，按质量百分比计为，盐化工生产工业石碱后排出的废渣碱渣98-99%，辅以除氯剂1-2%为100%为原材料，经混合搅拌均匀，制成微型细颗粒1-2mm，堆放固化，送入烘干窑经100摄氏度烘干脱除自由水和结晶水，即得水泥超细粉产品。2.根据权利要求1所述的水泥超细粉的制备方法，其特征在于，将水泥超细粉产品粉磨制成比表面积大于400-50...
【专利技术属性】
技术研发人员：谭纪林，华玉海，华建军，曹敏，谭伟，张会明，牛成，徐学成，陈阳，
申请(专利权)人：淮安市水泥厂有限公司，谭纪林，
类型：发明
国别省市：江苏,32