The invention provides an ink for the use of screen printing in the manufacture of electronic components. The ink can draw fine lines with high precision through screen printing and can perform screen printing continuously. The ink for screen printing of the invention contains the following surface modified silver nanoparticles (A) and the following solvent (B), and its viscosity (at 25 C and shear rate of 10 (1/s) is above 60 Pa.s. Surface Modified Silver Nanoparticles (A): Structures with silver nanoparticles coated by amine-containing protectants. Solvent (B): Solvents containing at least terpene solvents with boiling point below 130 C contain less than 20% of the total solvent weight.
【技术实现步骤摘要】
【国外来华专利技术】网版印刷用油墨
本专利技术涉及一种油墨，其用于使用网版印刷法来制造电子部件的用途。本申请主张了于2016年4月4日在日本提交的日本专利申请第2016-075037号的优先权，并将其内容引用于此。
技术介绍
由于银纳米粒子能够低温烧结，因此其可用于在塑料基板上形成电极或布线等电子部件的用途。然而，银纳米粒子存在容易凝聚的问题。专利文献1中公开了，通过用含胺保护剂包覆银纳米粒子的表面，可以在溶剂中获得良好的分散稳定性，并且将该银纳米粒子分散于包含脂环烃或醇等的溶剂中而得到的油墨适用于喷墨印刷。现有技术文献专利文献专利文献1：国际公开第2014/021270号
技术实现思路
专利技术要解决的技术问题然而，由于所述油墨的粘度对于网版印刷用途过低，因此容易模糊，难以高精度地绘制细线。此外，在网版印刷的情况下，存在如下问题：印刷后油墨残留在丝网中，但当该残留油墨中含有高挥发性醇等溶剂时，由于所述溶剂挥发，油墨发生增粘或者干燥固结，造成网孔堵塞，使得连续印刷变得困难。因此，本专利技术的一个目的是提供一种油墨，其用于通过网版印刷法制造电子部件的用途，该油墨能够通过网版印刷绘制高精度的...
【技术保护点】
1.一种网版印刷用油墨，其含有下述表面改性银纳米粒子(A)和下述溶剂(B)，该网版印刷用油墨的粘度(在25℃、剪切速度10(1/s)下)为60Pa·s以上，表面改性银纳米粒子(A)：具有银纳米粒子的表面由含胺保护剂进行了包覆的结构，溶剂(B)：至少含有萜烯类溶剂，并且沸点低于130℃的溶剂的含量为溶剂总量的20重量％以下。
【技术特征摘要】
【国外来华专利技术】2016.04.04 JP 2016-0750371.一种网版印刷用油墨，其含有下述表面改性银纳米粒子(A)和下述溶剂(B)，该网版印刷用油墨的粘度(在25℃、剪切速度10(1/s)下)为60Pa·s以上，表面改性银纳米粒子(A)：具有银纳米粒子的表面由含胺保护剂进行了包覆的结构，溶剂(B)：至少含有萜烯类溶剂，并且沸点低于130℃的溶剂的含量为溶剂总量的20重量％以下。2.根据权利要求1所述的网版印刷用油墨，其中，保护剂中，作为胺，包含总碳原子数为6以上的脂肪族单胺(1)，并包含总碳原子数为5以下的脂肪族单胺(2)和/或总碳原子数为8以下的脂肪族二胺(3)。3.根据权利要求2所述的网版印刷用油墨，其中，总碳原子数为6以上的脂肪族单胺(1)为具有直链烷基且总碳原子数为6～18的单胺和/或具有支链烷基且总碳原子数为6～16的单胺。4.根据权利要求2或3所述的网版印刷油墨，其中，总碳原子数为5以下的脂肪族单胺(2)为具有直链或支链烷基且总碳原子数为2～5的单胺。5.根据权利要求2～4中任一项所述的网版印刷用油墨，其中，总碳原子数为8以下的脂肪族二胺(3)如下通式(a...