The invention discloses an acrylic glass UV ink coating. A acrylic glass UV ink coating is composed of four to five portions of organosilicon modified acrylic resin, 0.5 portions of UV initiator, 0.5 to 1.5 portions of butyl acetate, 0.3 to 0.7 portions of waterproofing agent, 0.3 to 0.7 portions of adhesion promoter and 2.0 to 3.0 portions of diluent. The adhesion promoter is a titanate coupling agent. The UV spray printing pattern of the ink coating on the acrylic glass material provided by the invention can not be pulled off by 3M adhesive tape, and the adhesion with the acrylic glass substrate is enhanced, the waterproof and weatherability are enhanced, and the adhesion of the UV spray painting on the acrylic glass is improved significantly.
【技术实现步骤摘要】
一种亚克力玻璃UV油墨涂层
：本专利技术涉及印刷油墨涂层
，具体涉及一种亚克力玻璃UV油墨涂层。
技术介绍
：UV(紫外光固化)油墨是指在紫外线照射下，利用不同波长和能量的紫外光使油墨连接料中的单体聚合成聚合物，使油墨成膜和干燥的油墨。UV印刷油墨也属于油墨，必须具备良好的印刷适性，适宜的固化干燥速率。同时具有良好的附着力，并具备耐磨、耐蚀、耐候等特性。现有的亚克力玻璃UV油墨涂层经过UV打印机喷墨后，附着力很差，使用在户外，被户外雨水一淋就会脱落，由于该UV印刷油墨涂层的使用效果特别高，所以迫切需要解决该技术问题。
技术实现思路
：本专利技术的目的是提供一种亚克力玻璃UV油墨涂层。本专利技术利用通过增加在亚克力玻璃UV油墨涂层配方中添加防水处理剂和附着力促进剂，显著提高印刷油墨涂层与亚克力玻璃基材的附着力。本专利技术是通过以下技术方案予以实现的：本专利技术的一个目的是提出一种亚克力玻璃UV油墨涂层，按质量份数计，包括如下组分：有机硅改性丙烯酸树脂4～5份、UV引发剂0.5份、醋酸丁酯0.5～1.5份、防水处理剂0.3～0.7份、附着力促进剂0.3～0.7份和稀...
【技术保护点】
1.一种亚克力玻璃UV油墨涂层，特征在于，按质量份数计，包括如下组分：有机硅改性丙烯酸树脂4～5份、UV引发剂0.5份、醋酸丁酯0.5～1.5份、防水处理剂0.3～0.7份、附着力促进剂0.3～0.7份和稀释剂2.0～3.0份，所述的防水处理剂为氨基有机硅防水处理剂，所述的附着力促进剂为钛酸酯偶联剂。
【技术特征摘要】
1.一种亚克力玻璃UV油墨涂层，特征在于，按质量份数计，包括如下组分：有机硅改性丙烯酸树脂4～5份、UV引发剂0.5份、醋酸丁酯0.5～1.5份、防水处理剂0.3～0.7份、附着力促进剂0.3～0.7份和稀释剂2.0～3.0份，所述的防水处理剂为氨基有机硅防水处理剂，所述的附着力促进剂为钛酸酯偶联剂。2.根据权利要求1所述的亚克力玻璃UV油墨涂层，其特征在于，所述的氨基有机硅防水处理剂由如下步骤制备而成：a、将0.3mol八甲基环四硅氧烷、1mol四乙烯基四甲氧基环四硅氧烷，在压力为0.75MPa条件下减压蒸馏脱除低沸物，再加入1molN-β-(氨乙基)-γ-氨丙基甲基二甲氧基硅烷和0.001mol氢氧化钾，常压下在130℃下反应10h，再升温至160℃，保持25min后在0.75MPa条件下减压蒸馏脱除低沸物，获得氨基有机硅中间体；b、...
【专利技术属性】
技术研发人员：黄颂，
申请(专利权)人：东莞市绿泉实业有限公司，
类型：发明
国别省市：广东,44