The invention discloses a plastic material for valve sealing ring, which is made of 60 70 parts of methyl trifluoropropyl silicone rubber, 30 40 parts of high degree polyethylene, 2 4 parts of zinc oxide, 1 4 parts of antioxidant RD, 2 4 parts of vulcanizing agent, 1 2 parts of vulcanizing aid and 1 2 parts of nano grade silicon dioxide. As a result of adopting the above technical scheme, the invention has the following beneficial effects: the formulation of the invention is reasonable, the raw materials are easy to obtain, the valve sealing ring produced by the plastic material of the invention has long service life, good anti-aging performance and strong corrosion resistance.
【技术实现步骤摘要】
一种阀门密封圈用塑胶料
本专利技术涉及一种密封圈，具体说是一种阀门密封圈用塑胶料。
技术介绍
密封圈又名O型密封圈，是一种用以密封作用的配件，对于密封圈的要求如下：除应具备密封圈材料的一般要求外，密封圈还要注意下述条件：(1)富有弹性和回弹性；(2)适当的机械强度，包括扩张强度、伸长率和抗撕裂强度等。(3)性能稳定，在介质中不易溶胀，热收缩效应（焦耳效应）小。(4)易加工成型，并能保持精密的尺寸。(5)不腐蚀接触面，不污染介质等。满足上述要求的最适合而且最常用的材料是橡胶，所以密封圈大多用橡胶材料制成。目前，由于橡胶密封圈的抗老化性能较差，因而大大缩短了密封圈的使用寿命，尤其是应用于阀门上的密封圈要求更高，除了抗老化性能，对其抗腐蚀能力也有较高的要求。
技术实现思路
本专利技术所要解决的技术问题是提供一种阀门密封圈用塑胶料。为解决上述技术问题，本专利技术的技术方案是：一种阀门密封圈用塑胶料，由以下重量份的原料制成：甲基三氟丙基硅橡胶60-70份，高聚合度聚乙烯30-40份，氧化锌2-4份，防老剂RD1-4份，硫化剂2-4份，助硫化剂1-2份，纳米级二氧化硅1-2份。作...
【技术保护点】
1.一种阀门密封圈用塑胶料，其特征在于，由以下重量份的原料制成：甲基三氟丙基硅橡胶60‑70份，高聚合度聚乙烯30‑40份，氧化锌2‑4份，防老剂RD 1‑4份，硫化剂2‑4份，助硫化剂1‑2份，纳米级二氧化硅1‑2份。
【技术特征摘要】
1.一种阀门密封圈用塑胶料，其特征在于，由以下重量份的原料制成：甲基三氟丙基硅橡胶60-70份，高聚合度聚乙烯30-40份，氧化锌2-4份，防老剂RD1-4份，硫化剂2-4份，助硫化剂1-2份，纳米级二氧化硅1-2份。2.根据权利要求1所述的一种阀门密封圈用塑胶料，其特征在于，由以下重量份的原料制成：甲基三氟丙基硅橡胶60份，高聚合度聚乙烯30份，氧化锌2份，防老剂RD1份，硫化剂2份，助硫化剂1份，纳米级二氧化硅1份。...