压敏型乳液胶黏剂制造技术

本发明专利技术涉及一种压敏型乳液胶黏剂，是在可聚合乳化剂存在下由含C4~12烷基丙烯酸酯的单体在水介质中聚合得到的。主要用于制压敏胶带。其特征在于：先将40份水、0.2份过硫酸铵、2份丙烯酸丁酯和2份可聚合乳化剂装入反应罐中，混合均匀，升温至82℃。将剩余的物料混合均匀，并用氨水调ph至中性，然后逐滴加到82℃的反应罐内。加料完毕，在82℃搅拌，得到黏度为4pa·s的乳液胶黏剂。

Pressure sensitive emulsion adhesive

The invention relates to a pressure sensitive emulsion adhesive, which is polymerized in a water medium by a monomer containing C4~12 alkyl acrylate in the presence of polymerizable emulsifiers. Mainly used for pressure sensitive tape. The characteristics are as follows: 40 phr of water, 0.2 phr of ammonium persulfate, 2 phr of butyl acrylate and 2 phr of polymerizable emulsifier are first put into the reaction tank, and the mixture is uniform, and the temperature is raised to 82 C. The remaining materials are mixed evenly, and the ammonia water is used to adjust the pH to neutral, and then added to the reaction tank at 82 C drop by drop. The emulsion adhesive with viscosity of 4pa? S was obtained after mixing and stirring at 82 C.

【技术实现步骤摘要】
压敏型乳液胶黏剂
本专利技术涉及一种压敏型乳液胶黏剂及其制备方法，属于精细化工

技术介绍
压敏型乳液胶黏剂系以丙烯酸丁酯、聚氧乙烯月桂醇醚硫酸铵、丙烯酰胺、过硫酸铵、聚合乳化剂、水、丙烯酸、氨水等为原料经合理配制而成。压敏型乳液胶黏剂是胶粘剂的一种新产品，其主要特点为：原料易得，工艺简单，保存期长，使用方便，粘结牢固，该压敏胶是在可聚合乳化剂存在下由含C4~12烷基丙烯酸酯的单体在水介质中聚合得到的。主要用于制压敏胶带。本压敏型乳液胶黏剂的配比还没有见诸科技文献的报道。
技术实现思路
本专利技术需要解决的技术问题就在于克服现有技术的缺陷，提供一种压敏型乳液胶黏剂及其制备方法，它原料易得，工艺简单，保存期长，使用方便，粘结牢固，该压敏胶是在可聚合乳化剂存在下由含C4~12烷基丙烯酸酯的单体在水介质中聚合得到的。主要用于制压敏胶带。为解决上述问题，本专利技术采用如下技术方案：本专利技术公开了一种压敏型乳液胶黏剂制备方法，所述的压敏型乳液胶黏剂由下列重量份配比的原料制备而成丙烯酸丁酯49.2%～51%、聚氧乙烯月桂醇醚硫酸铵0.523%～0.6%、丙烯酰胺0.523%～0.6%、过硫本文档来自技高网...

【技术保护点】
1.一种压敏型乳液胶黏剂，本专利技术是在可聚合乳化剂存在下由含C4~12烷基丙烯酸酯的单体在水介质中聚合得到的，主要用于制压敏胶带。

【技术特征摘要】
1.一种压敏型乳液胶黏剂，本发明是在可聚合乳化剂存在下由含C4~12烷基丙烯酸酯的单体在水介质中聚合得到的，主要用于制压敏胶带。2.一种压敏型乳液胶黏剂制备方法，其特征在于，所述压敏型乳液胶黏剂由下列重量份配比的原料制备而成：丙烯酸丁酯49.28%、聚氧乙烯月桂醇醚硫酸铵0.53%、丙烯酰胺0.53%、过硫酸铵0.11%、聚合乳化剂1.07...