The invention relates to a high softening point wax and a preparation method thereof, belonging to the technical field of chemical industry. The high softening point wax includes polyethylene oligomer, polypropylene wax and industrial hydrogenated oil. The softening point of polyethylene oligomer is more than 110 C, and the average molecular weight is 2000 5000. The high softening point wax of the invention is mainly used as a lubricating dispersant in the production process of plastic products, and has the characteristics of concentrated effective molecular weight, which helps to improve the dispersion effect and coloring power. Softening point can reach 120 C. It has excellent heat resistance and thermal stability. It has good compatibility and fluidity in the production of color masterbatch. It strengthens the lubrication performance, improves the production efficiency, makes the product easier to demould and improves the surface finish of the product.
【技术实现步骤摘要】
一种高软化点蜡及其制备方法
本专利技术涉及一种高软化点蜡及其制备方法，属于化工
技术介绍
聚乙烯蜡作为润滑分散剂被大量的使用在塑料生产工艺过程中。现有的聚乙烯蜡制备方法一般采用大分子量的聚乙烯经过一系列工艺步骤制成，其制造成本高，且生产出来的聚乙烯蜡分子量分布较宽，导致分散效果和作色性能降低。而且，其软化点和硬度等数据得不到有效保证。
技术实现思路
针对上述问题，本专利技术提出了一种成本低、软化点高、黏度性能好，同时具有优良的外部润滑和较强的内部润滑作用，且分散性好的高软化点蜡及其制备方法。为解决上述技术问题，本专利技术的技术方案为：一种高软化点蜡，包括：聚乙烯低聚物、聚丙烯蜡和工业氢化油；所述高软化点蜡的各组分质量比为：聚乙烯低聚物40-50%、聚丙烯蜡20-30%、工业氢化油40-20%。所述聚乙烯低聚物的软化点大于110℃，其平均分子量为2000-5000。所述工业氢化油的主要成分为饱和脂肪酸甘油酸酯（脂肪酸为硬脂酸），常温下外观为白色或微黄色蜡状固体。一种高软化点蜡的制备方法，包括如下步骤：1）将聚乙烯低聚物破碎并投入反应釜中；2）加热聚乙烯低聚物直...
【技术保护点】
1.一种高软化点蜡，其特征在于，包括：聚乙烯低聚物、聚丙烯蜡和工业氢化油；所述高软化点蜡的各组分质量比为：聚乙烯低聚物40‑50%、聚丙烯蜡20‑30%、工业氢化油40‑20%。
【技术特征摘要】
1.一种高软化点蜡，其特征在于，包括：聚乙烯低聚物、聚丙烯蜡和工业氢化油；所述高软化点蜡的各组分质量比为：聚乙烯低聚物40-50%、聚丙烯蜡20-30%、工业氢化油40-20%。2.根据权利要求1所述的一种高软化点蜡，其特征在于，所述聚乙烯低聚物的软化点大于110℃，其平均分子量为2000-5000。3.一种高软化点蜡的制备方法，其特征在于，包括如下步骤：1）将聚乙烯低聚物破碎并投入反应釜中...