The invention discloses a waterproof ceramic tile adhesive, which comprises 30-40 portions of Portland cement, 30-40 portions of quartz sand, 15-20 portions of modified fly ash, 10-15 portions of modified wollastonite fiber, 5-10 portions of carboxymethyl vitamin, 5-10 portions of kapok fiber, 1-5 portions of seaweed gum powder, 0.5-1 portions of latex powder and thickening. The modified wollastonite fibers are prepared by mixing wollastonite fibers with cyclodextrin and graphene and adding them to cationic surfactant solution by ultrasonic mixing for 10-20 minutes. The product of the invention has good flexibility and bonding strength, effectively prevents moisture from penetrating into the base material through the cracks of bricks, protects the firmness of ceramic tiles, and improves the stability and waterproof performance of the decoration system.
【技术实现步骤摘要】
一种防水瓷砖胶黏剂
本专利技术属于瓷砖胶粘剂领域，特别涉及一种防水瓷砖胶黏剂。
技术介绍
瓷砖胶粘剂，是一种粘结度高、耐水、耐冻、耐老化的胶粘剂，主要用于粘贴普通瓷砖、陶砖、釉面砖、地砖、大理石、花岗石、石膏板等墙体装饰材料。目前，市场上的瓷砖胶粘剂的种类繁多，不同的应用对瓷砖胶粘剂的性能要求不同，如长期应用在碱性环境中的，要求瓷砖胶抗碱性能强；粘贴大尺寸砖在立面的，要求抗滑移性能强的瓷砖胶；粘贴低吸水率大尺寸玻化砖的，要求瓷砖胶具备较好的润湿性能；长期遇水的环境，要求使用具有一定防水性能的瓷砖胶。目前，常用的瓷砖胶粘剂对防水性能的要求比较低，只对浸水后的粘结强度进行了限定，而对吸水率和抗渗性能没有任何要求，但在实际使用过程中，瓷砖胶的防水性能很关键，例如浴室，经常迎水面遇水，若瓷砖胶不具有防水抗渗性能，水会顺着瓷砖缝隙渗透到瓷砖胶层，在瓷砖胶层横向扩散到下面的防水层，使防水层造成了长期潮湿遇水的环境，导致防水层柔韧性、粘结力、防水性能都会有所下降，长此以往会有潮气甚至水透过墙体，影响墙面的装修和居住舒适度。因此，研究具有防水抗渗性能的瓷砖胶黏剂具有重要的现实意义...
【技术保护点】
1.一种防水瓷砖胶黏剂，其特征在于，包括如下重量份的原料：硅酸盐水泥30～40份，石英砂30～40份，改性粉煤灰15～20份，改性硅灰石纤维10～15份，羧甲基维生素5～10份，木棉纤维5～10份，海菜胶粉1～5份，乳胶粉0.5～1份，增稠剂0.1～0.5份，交联剂0.1～0.5份。
【技术特征摘要】
1.一种防水瓷砖胶黏剂，其特征在于，包括如下重量份的原料：硅酸盐水泥30～40份，石英砂30～40份，改性粉煤灰15～20份，改性硅灰石纤维10～15份，羧甲基维生素5～10份，木棉纤维5～10份，海菜胶粉1～5份，乳胶粉0.5～1份，增稠剂0.1～0.5份，交联剂0.1～0.5份。2.根据权利要求1所述的防水瓷砖胶黏剂，其特征在于，包括如下重量份的原料：硅酸盐水泥40份，石英砂30份，粉煤灰15份，硅灰石纤维10份，羧甲基维生素8份，木棉纤维5份，海菜胶粉3份，乳胶粉1份，增稠剂0.5份，交联剂0.3份。3.根据权利要求1所述的防水瓷砖胶黏剂，其特征在于，所述改性硅灰石纤维通过如下方法制备所得：将硅灰石...
【专利技术属性】
技术研发人员：刘冠麟，黎家国，张涛，樊哲新，
申请(专利权)人：云南欣城防水科技有限公司，
类型：发明
国别省市：云南,53
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。