The invention provides a composite flocculant for sewage, which is calculated by weight, including the following components: polyferric chloride and organic composite flocculant 40-60 phr, fly ash modified polyferric sulfate 10-20 phr, sodium dodecylbenzene sulfonate 15-25 phr, sodium petroleum sulfonate 20-30 phr, starch 10-20 phr, sodium carboxymethylcellulose. 8-12 copies, 6-10 copies of quaternary ammonium salt; polyferric chloride and organic composite flocculant were mainly prepared from ferric chloride, aluminium chloride and carboxylated chitosan. The flocculating agent has simple preparation, fast flocculation rate, high turbidity removal rate, high decolorization rate and high COD removal rate.
【技术实现步骤摘要】
污水用复合絮凝剂
本专利技术属于絮凝剂
，具体涉及一种污水用复合絮凝剂。
技术介绍
随着人们环保意识的增强，工业废水、城市污水的达标处理成为当务之急。根据调查，目前工业废水处理量还不到总量的20％，城市污水暂时仅在少数城市进行实验性处理，主要原因是处理费用高。因此，开发高效、廉价的废水处理剂刻不容缓。絮凝剂是最重要的水处理剂，它用量极大，每年以很高的百分比递增。对于生活污水及大部分的工业污水，其主要的污染因子主要由污水中的颗粒物(微小颗粒物)引起，而这些颗粒物在电位场的影响下，相当稳定，很难相互结合成团而沉淀或上浮。投加的絮凝剂的作用在于：絮凝剂溶于水，并在适当的水力搅拌的条件下，污水中微小颗粒物的电位场会得到中和，颗粒物间的静电斥力减弱，同时在水力搅拌条件下，颗粒物相互碰撞的机率增加，微小颗粒物会相互结合成小絮体，此即为压缩双电层过程。但结合后的微小絮体的电位场会随着絮体的形成而又增大，从而阻止小絮体进一步结合成大絮体。传统絮凝剂聚丙烯酰胺虽可解决上述问题，但由于聚丙烯酰胺溶于水后是长链结构且基本是直链结构，无法形成复杂的空间三维结构，吸附微小颗粒物及溶解...
【技术保护点】
1.一种污水用复合絮凝剂，其特征在于，按照重量份数计算，包括以下组分：聚合氯化铁‑有机复合絮凝剂40～60份，粉煤灰改性聚合硫酸铁10～20份，十二烷基苯磺酸钠15～25份，石油磺酸钠20～30份，淀粉10～20份，羧甲基纤维素钠8～12份，季铵盐6～10份；所述聚合氯化铁‑有机复合絮凝剂主要由三氯化铁、氯化铝与羧基化壳聚糖制备得到。
【技术特征摘要】
1.一种污水用复合絮凝剂，其特征在于，按照重量份数计算，包括以下组分：聚合氯化铁-有机复合絮凝剂40～60份，粉煤灰改性聚合硫酸铁10～20份，十二烷基苯磺酸钠15～25份，石油磺酸钠20～30份，淀粉10～20份，羧甲基纤维素钠8～12份，季铵盐6～10份；所述聚合氯化铁-有机复合絮凝剂主要由三氯化铁、氯化铝与羧基化壳聚糖制备得到。2.根据权利要求1所述的污水用复合絮凝剂，其特征在于，所述聚合氯化铁-有机复合絮凝剂的制备方法包括以下步骤：将三氯化铁、氯化铝加入至羧基化壳聚糖的水溶液中，搅拌均匀，然后滴加碳酸氢钠溶液至碱化度为0.5～1.5，然后加入丙烯酰胺，再加入稳定剂Na2HPO4继续搅拌一定的时间，自然冷却至室温即可。3.根据权利要求2所述的污水用复合絮凝剂，其特征在于，所述三氯化铁、氯化铝...
【专利技术属性】
技术研发人员：汪泽维，汪鹏，
申请(专利权)人：芜湖市棠华建材科技有限公司，
类型：发明
国别省市：安徽,34
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。