The present invention relates to a standard nuts rust removal solution formulation, which is characterized by: hexamethylenetetramine 15_20 phr, diethylthiophosphate 15_18 phr, sodium dioctylsuccinate 8_10 phr, benzoic acid 1_4 phr, potassium chloride 1_2 phr, hydrochloric acid 5 to 10 phr, citric acid 6 to 12 phr, tartaric acid 2 to 8 phr, hydroxyacetic acid 1 to 5 phr acid. The rust removal solution of the invention consists of water-based solvent, anionic surfactant and sodium tripolyphosphate, chitosan 2-6, polyethylene glycol 4-10, deionized water 50-70; the rust removal solution of the invention is composed of water-based solvent, and anionic surfactant is composed of 0.5-1.5 parts of oxidized starch, 10-20 parts of trimethylhexadecyl ammonium bromide, 1-5 parts of sodium tripolyphosphate, 2-6 parts of chitosan, 4-10 parts of polyethylene glyc As the main ingredient, the cleaning effect is better, and it will not corrode industrial pipelines, reduce environmental pollution, and be more environmentally friendly.
【技术实现步骤摘要】
一种标准螺母除锈液配方
本专利技术涉及金属除锈领域，尤其涉及一种标准螺母除锈液配方。
技术介绍
黑色金属(钢材)置于室外或露天条件下容易生锈，不但影响外观质量，还会影响喷漆、粘接等工艺的正常进行，如不及时处理，更会造成材料的报废，导致不必要的经济损失。传统的化学除锈通常使用强酸，酸能与铁锈及金属氧化物发生化学反应，生成可溶性盐类，从而达到除锈的目的，除锈的同时，酸又能和基础金属发生反应放出氢，氢能对铁锈和难溶的氧化皮产生压力，有利于他们的剥落和高价铁的还原，加速酸洗的过程。但传统的酸液处理方法也存在着明显的缺陷：即处理过程中大量氢气的产生会使钢材产生氢脆现象，引起金属的力学性能下降，影响钢铁本身的强度；同时易形成酸雾，影响操作人员的健康和腐蚀周围的设备及环境；酸液的消耗量也较大，增加处理成本；这类酸会对钢材形成过腐蚀。此外大量产生的残渣，需经常排放，既严重腐蚀工业管道，又污染土壤和环境。
技术实现思路
本专利技术要解决的技术问题是提供一种标准螺母除锈液配方，能够解决一般的除锈液清洗效力差、直接排液容易导致污染的问题。为解决上述技术问题，本专利技术的技术方案为：一种标准...
【技术保护点】
1. 一种标准螺母除锈液配方，其特征在于：包括六亚甲基四胺15‑20 份、二乙基硫代磷酸酯15‑18份、二辛基琥珀酸磺酸钠8‑10份、苯甲酸1‑4份、氯化钾1‑2份、盐酸5～10份、柠檬酸6～12份、酒石酸2～8份、羟基乙酸1～5份、十二烷基硫酸钠6～14份、聚天冬氨酸4～8份、氧化淀粉0.5～1.5份、三甲基十六烷基溴化铵10～20份、三聚磷酸钠1～5份、壳聚糖2～6份、聚乙二醇4～10份、去离子水50～70份。
【技术特征摘要】
1.一种标准螺母除锈液配方，其特征在于：包括六亚甲基四胺15-20份、二乙基硫代磷酸酯15-18份、二辛基琥珀酸磺酸钠8-10份、苯甲酸1-4份、氯化钾1-2份、盐酸5～10份、柠檬酸6～12份、酒石酸2～...
【专利技术属性】
技术研发人员：黄仁秀，
申请(专利权)人：如皋市跃天特种标准件有限公司，
类型：发明
国别省市：江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。