The invention discloses a flame retardant sheath material for track traffic cables and a preparation method thereof. One kind of flame retardant sheath material for rail transit cable is composed of 80-90 phr of polyethylene, 30-40 phr of EVA resin, 10-15 phr of compatibilizer, 1-2 phr of rheological agent, 3-8 phr of phosphorous flame retardant plasticizer, 10-30 phr of ammonium polyphosphate, 30-60 phr of expandable graphite, 3-8 phr of antioxidant and 1-3 phr of processing aids. The sheath material of the invention has excellent comprehensive performance, not only excellent insulation performance and high temperature resistance, but also good wear resistance, climate aging resistance, ozone aging resistance, ultraviolet radiation resistance, oil resistance, acid and alkali resistance, etc. It is durable, completely reliable and has broad application prospects.
【技术实现步骤摘要】
一种轨道交通电缆用阻燃护套料及其制备方法
本专利技术属于轨道交通电缆材料领域,具体涉及一种轨道交通电缆用阻燃护套料及其制备方法。
技术介绍
电缆护套是电缆不可缺少的中间结构部分，起着保护电缆的作用，保证电缆的通电安全，让铜丝和水、空气等介质隔绝，避免出现漏电现象。随着机车的快速发展，铁路市场对轨道交通用电缆提出更高的要求，如耐温等级、耐老化性、耐油性、耐磨性、阻燃性等。
技术实现思路
本专利技术提供了一种轨道交通电缆用阻燃护套料及其制备方法，以解决上述技术问题。为了解决上述技术问题，本专利技术采用的技术方案是：一种轨道交通电缆用阻燃护套料，由以下原料按重量份组成：由以下原料按重量份组成：聚乙烯80～90份、EVA树脂30～40份、相容剂10～15份、流变剂1～2份、磷系阻燃增塑剂3～8份、聚磷酸铵10～30份、可膨胀石墨30～60份、抗氧剂3～8份、加工助剂1～3份。优选的，一种轨道交通电缆用阻燃护套料，由以下原料按重量份组成：聚乙烯80份、EVA树脂30份、相容剂10份、流变剂1份、磷系阻燃增塑剂3份、聚磷酸铵10份、可膨胀石墨30份、抗氧剂3份、加工助剂1份。优选...
【技术保护点】
1.一种轨道交通电缆用阻燃护套料，其特征在于，由以下原料按重量份组成：聚乙烯80～90份、EVA树脂30～40份、相容剂10～15份、流变剂1～2份、磷系阻燃增塑剂3～8份、聚磷酸铵10～30份、可膨胀石墨30～60份、抗氧剂3～8份、加工助剂1～3份。
【技术特征摘要】
1.一种轨道交通电缆用阻燃护套料，其特征在于，由以下原料按重量份组成：聚乙烯80～90份、EVA树脂30～40份、相容剂10～15份、流变剂1～2份、磷系阻燃增塑剂3～8份、聚磷酸铵10～30份、可膨胀石墨30～60份、抗氧剂3～8份、加工助剂1～3份。2.根据权利要求1所述的轨道交通电缆用阻燃护套料，其特征在于，由以下原料按重量份组成：聚乙烯80份、EVA树脂30份、相容剂10份、流变剂1份、磷系阻燃增塑剂3份、聚磷酸铵10份、可膨胀石墨30份、抗氧剂3份、加工助剂1份。3.根据权利要求1所述的轨道交通电缆用阻燃护套料，其特征在于，由以下原料按重量份组成：聚乙烯85份、EVA树脂35份、相容剂12.5份、流变剂1.5份、磷系阻燃增塑剂5...
【专利技术属性】
技术研发人员：毕力，高敏，陈鹏，刘勇，
申请(专利权)人：安徽意力电缆有限公司，
类型：发明
国别省市：安徽,34