The invention discloses a chitosan iodine biomaterial with sterilization and killing pathogenic microorganisms. Its main components and mass fraction are: iodine 0.05%-1%; potassium iodide 0.1%-0.5%; potassium iodate 0.15%-0.4%; glycerol 1%-4%; boric acid 0.1-0.2%; polyvinylpyrrolidone 5%-15%; water-soluble chitosan 0.1%-1.0%; algae. Sodium 0.1%-1.0%; calcium bicarbonate 0.05%-1.0%; tea polyphenols 0.1%-0.4%; phosphate buffer 5.0%-8.0%; add water for injection or purified water to sufficient amount. This product has no toxicity, irritation, sensitization to human body, good biodegradability and biocompatibility, good sterilization, wound repair and preventive medical biomaterials to prevent implantable metastasis caused by tumor cells scattered in the inner membrane of human body cavity during cancer surgery.
【技术实现步骤摘要】
几丁聚糖碘生物材料及其制备方法
本专利技术涉及一种围手术期使用的、医用杀菌、抗菌、防粘连、生物材料及皮肤及黏膜外用消毒及术野皮肤粘膜生物材料，具体涉及几丁聚糖碘生物材料及其制备方法。
技术介绍
目前传统制备含碘制剂主要为聚乙烯醚和聚乙烯吡咯烷酮包埋碘制剂，这种碘制剂存在缺陷在于高能度碘可以长期保存，但低于5000PPm碘溶液有效碘容易挥发。制备成碘酒酊剂效果很好但对皮肤、粘膜刺激性大。低浓度几丁聚糖碘微球溶胶液制剂目前依然是一空白。在外科感染性手术如肠穿孔，为了防止术后感染一般采取临床使用生理盐水或注射用水临时稀释碘伏溶液液在用于腹腔及感染创面冲洗。临时配制一方面使用不方便，另一方面容易造成二次污染。目前，围手术期一些感染性患者如肠穿孔患者造成腹腔感染，手术使用生理盐水很难预防感染，临床医生使用外用碘伏溶液类的药主要有聚乙烯吡咯烷酮～I液(PVP～I)、聚乙二醇～I(PEG～I)等使用生理盐水进行稀释后冲洗腹腔，很不方便，同时配制时容易造成二次污染。由于聚乙烯吡咯烷酮～I液(PVP～I)、聚乙二醇～I(PEG～I)低浓度溶液极不稳定、有效碘极易挥发。临床上一种既能...
【技术保护点】
1.几丁聚糖碘生物材料，其特征在于：该生物材料主要成份及其质量分数为：碘 0.05%～1%；碘化钾 0.1%～0.5%；碘酸钾 0.15%～0.4%；甘油 1%～4%；硼酸 0.1～0.2%；聚乙烯吡咯烷酮 5%～15%；水溶性壳聚糖 0.1%～1.0%；海藻酸钠 0.1%～1.0%；碳酸氢钙 0.05%～1.0%；茶多酚 0.1%～0....
【技术特征摘要】
1.几丁聚糖碘生物材料，其特征在于：该生物材料主要成份及其质量分数为：碘0.05%～1%；碘化钾0.1%～0.5%；碘酸钾0.15%～0.4%；甘油1%～4%；硼酸0.1～0.2%；聚乙烯吡咯烷酮5%～15%；水溶性壳聚糖0.1%～1.0%；海藻酸钠0.1%～1.0%；碳酸氢钙0.05%～1.0%；茶多酚0.1%～0.4%；磷酸缓冲盐5.0%～8.0%；加注射用水或纯化水至足量。2.一种如权利要求1所述的几丁聚糖碘生物材料的制备方法，其特征在于：按如下步骤制备：步骤1）取碘化钾、碘酸钾用注射用水或纯化水溶解...