本发明专利技术公开了一种含有聚丙烯纤维的抗裂砂浆及其在制备管廊中的应用。以重量份计，原料组成包括：普通硅酸盐水泥100份、砂300‑350份、羟丙基甲基纤维素醚0.1‑0.3份、纳米蒙脱石0.1‑0.2份、纳米凹凸棒土0.1‑0.2份、硅藻土0.1‑0.2份、木薯淀粉0.1‑0.2份、玉米淀粉0.1‑0.2份、聚丙烯纤维1‑2份、硫铝酸钙0.1‑0.2份、减水剂1.5‑2份。本发明专利技术还公开了其应用。本发明专利技术提供了一种强度高、抗裂性能优异的含有聚丙烯纤维的抗裂砂浆及其在制备管廊中的应用。

A crack resistant mortar containing polypropylene fiber and its application in pipe gallery construction

The invention discloses a crack resistant mortar containing polypropylene fiber and its application in the preparation of pipe corridors. By weight, the raw materials consist of 100 Portland cement, 300 350 sand, 0.1 0.3 hydroxypropyl methyl cellulose ether, 0.1 0.2 nano-montmorillonite, 0.1 0.2 nano-attapulgite, 0.1 0.2 diatomite, 0.1 0.2 cassava starch, 0.1 0.2 corn starch, 1 0.2 polypropylene fiber, 1 0.2 sulfur. Calcium aluminate 0.1, 0.2, and water reducing agent 1.5, 2. The invention also discloses its application. The invention provides a crack resistant mortar containing polypropylene fiber with high strength and excellent crack resistance and its application in preparing pipe gallery.

【技术实现步骤摘要】
一种含有聚丙烯纤维的抗裂砂浆及其在制备管廊中的应用
本专利技术涉及建筑材料，尤其涉及一种含有聚丙烯纤维的抗裂砂浆及其在制备管廊中的应用。
技术介绍
砂浆是建筑上砌砖使用的黏结物质，由一定比例的沙子和胶结材料(水泥、石灰膏、黏土等)加水和成，也叫灰浆，也作沙浆。通过在砂浆中添加外加剂能够改善砂浆的性能，外加剂的种类多种多样，主要包括防冻剂、减水剂、保水剂、增强剂、抗菌剂等，外加剂的种类、含量会直接影响砂浆的性能，尽管现有技术中已经做出了很多相关的研究，但是仍然存在很多问题，砂浆的抗裂性能及强度仍有提升的空间。
技术实现思路
为解决现有技术中的问题，本专利技术提供了一种强度高、抗裂性能优异的含有聚丙烯纤维的抗裂砂浆及其在制备管廊中的应用。一种含有聚丙烯纤维的抗裂砂浆，以重量份计，原料组成包括：优选的，所述的含有聚丙烯纤维的抗裂砂浆，以重量份计，原料组成包括：优选的，所述聚丙烯纤维为不同长度级配，其中以质量百分比计，长度4-6mm占比30％，7-10mm占比60％，11-13mm占比10％。优选的，所述聚丙烯纤维为经改性得到，改性方法包括：将85重量份聚丙烯、5重量份聚丙烯接枝马来酸酐、4重量本文档来自技高网...

【技术保护点】
1.一种含有聚丙烯纤维的抗裂砂浆，其特征在于，以重量份计，原料组成包括：

【技术特征摘要】
1.一种含有聚丙烯纤维的抗裂砂浆，其特征在于，以重量份计，原料组成包括：2.根据权利要求1所述的含有聚丙烯纤维的抗裂砂浆，其特征在于，以重量份计，原料组成包括：3.根据权利要求1所述的含有聚丙烯纤维的抗裂砂浆，其特征在于，所述聚丙烯纤维为不同长度级配，其中以质量百分比计，长度4-6mm占比30％，7-10mm占比60％，11-13mm占比10％。4.根据权利要求1所述的含有聚丙烯纤维的抗裂砂浆，其特征在于，所述聚丙烯纤维为经改性得到，改性方法包括：将85重量份聚丙烯、5...