The invention relates to fabric processing and provides a finishing process for elastic and super-flexible polyester fabric with good elasticity, softness and handle after processing. The process comprises the following steps: firstly, the fabric is mercerized by using a cloth mercerizing machine without spraying; secondly, the fabric obtained by the previous step is mercerized. High temperature setting machine is used to finalize the fabric. Finally, the fabric which has been finalized at high temperature in the previous step is loosely softened by open-width loose air-blast softening machine, and the finished product is obtained.
【技术实现步骤摘要】
无弹涤面料加工为有弹超柔面料的整理工艺本专利技术涉及面料加工,特别涉及一种无弹涤面料加工为有弹超柔面料的整理工艺。传统的不含氨纶的涤纶面料都不具有弹性,其一般是经过加工整理后使其具有一定弹性。现有的加工整理工艺通常是采用以下几个步骤来完成的:1)对面料进行丝光操作,即使用布铗丝光机,打开喷淋对面料进行丝光操作,其工艺参数为烧碱为240g/L;调整轧车压力为0.3MP,张力为0.3MP;布铗门幅为成品门幅;直辊去碱温度控制在90-95℃,车速控制在45-50m/min。2)将上一步骤处理后的面料利用高温定型机进行定型,其工艺参数为温度控制在210℃,车速控制在45-50m/min,面料超喂1-2%,高温定型机的门幅比进布门幅大1-2cm。3)将上一步骤定型后得到的面料利用低温拉幅机进行柔软拉幅,其工艺参数为温度控制在130-140℃,车速控制在45-50m/min,低温拉幅机的门幅比进布门幅大1-2cm,低温拉幅机上处理液的配方为:氨基硅油20g/L、阳离子软片5g/L。通过以上三个步骤处理使得不含氨纶的涤纶面料由不具有弹性改变为拉伸率3-4%,伸长率0.2-0.4%的有弹涤纶面料。但是此种工艺得到的面料其弹性较差,柔软性差,不能满足人们的要求,虽有制造商针对此性能去研究改变其处理工艺,但仍未能有效的提高该面料的弹性和柔软度。因此,针对上述的问题,本专利技术提出一种弹性好,柔软度高,手感好的无弹涤面料加工为有弹超柔面料的整理工艺。为解决此技术问题,本专利技术采取以下方案:一种无弹涤面料加工为有弹超柔面料的整理工艺,其特征在于:它包括如下步骤,(1)、丝光,采用 ...
【技术保护点】
1.一种无弹涤面料加工为有弹超柔面料的整理工艺,其特征在于:它包括如下步骤,(1)、丝光,采用布铗丝光机,通过控制门幅,不开喷淋对面料进行丝光操作;(2)、定型,将经上一步骤处理得到的面料利用高温定型机通过控制门幅进行定型;(3)、松式柔软,将经上一步骤高温定型后的面料利用平幅松式鼓风柔软机进行松式柔软,得到成品。
【技术特征摘要】
1.一种无弹涤面料加工为有弹超柔面料的整理工艺,其特征在于:它包括如下步骤,(1)、丝光,采用布铗丝光机,通过控制门幅,不开喷淋对面料进行丝光操作;(2)、定型,将经上一步骤处理得到的面料利用高温定型机通过控制门幅进行定型;(3)、松式柔软,将经上一步骤高温定型后的面料利用平幅松式鼓风柔软机进行松式柔软,得到成品。2.根据权利要求1所述的无弹涤面料加工为有弹超柔面料的整理工艺,其特征在于:所述步骤(1)中布铗丝光机的工艺参数为烧碱浓度260g/L,轧车压力为0.15MP,轧车...
【专利技术属性】
技术研发人员:徐建海,
申请(专利权)人:如皋市海鑫织造有限公司,
类型:发明
国别省市:江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。