一种改善高炉喷吹用煤粉流动性的添加剂及其使用方法技术

本发明专利技术属于高炉炼铁技术领域，尤其涉及一种改善高炉喷吹用煤粉流动性的添加剂及其使用方法。具体为将干燥后的冶金除尘灰与煤粉混合均匀后从高炉煤枪喷入高炉内部。本方法不但能够改善喷吹用煤粉的流动性能，还可增加高炉炼铁含铁矿物来源，从而实现煤粉的稳定喷吹，降低生产成本。

Additive for improving pulverized coal fluidity of blast furnace injection and use method thereof

The invention belongs to the technical field of blast furnace ironmaking, in particular to an additive for improving the fluidity of pulverized coal for blast furnace injection and its use method. Specifically, after mixing the dry metallurgical dust and the coal powder, the blast furnace is injected into the blast furnace by the coal gun. This method can not only improve the fluidity of pulverized coal for injection, but also increase the source of iron ore in blast furnace, so as to realize stable pulverized coal injection and reduce production cost.

【技术实现步骤摘要】
一种改善高炉喷吹用煤粉流动性的添加剂及其使用方法
本专利技术属于高炉炼铁
，尤其涉及一种改善高炉喷吹用煤粉流动性的添加剂及其使用方法。
技术介绍
高炉喷吹用煤粉的流动性属于煤粉的基础特性，反映了高炉喷煤过程中粉体输送性能的好坏。良好的输送性能是在喷煤过程中保持均匀和稳定喷煤量的前提条件。目前为降低生产成本，廉价的、流动性差的煤种大量的进行高炉喷吹，但当煤粉的流动性差时，会出现堵枪、空枪以及喷嘴堵塞等异常现象，造成喷煤量的剧烈波动和喷煤过程的不均匀，喷煤量经常波动会影响喷吹效果，降低喷入炉内煤粉的燃烧率，破坏炉况稳定，进而影响高炉生产顺行。因此，改善高炉喷吹用煤粉流动性具有重要的现实意义。
技术实现思路
针对现存的技术问题，本专利技术提供一种改善高炉喷吹用煤粉流动性的添加剂及其使用方法。不但能够改善高炉喷吹用煤粉的流动性，还可增加高炉炼铁含铁矿物来源，以解决大量使用廉价煤种导致的流动性差问题，从而实现粉体的稳定喷吹，达到提高煤比、降低成本的目的。具体技术方案如下：一种改善喷吹用煤粉流动性的添加剂，所述添加剂为冶金除尘灰，所述冶金除尘灰组分及重量百分比如下：40％≤TFe≤62％，0≤本文档来自技高网...

【技术保护点】
1.一种改善喷吹用煤粉流动性的添加剂，其特征在于，所述添加剂为冶金除尘灰，所述冶金除尘灰组分及重量百分比如下：40％≤TFe≤62％，0≤C≤30％，0≤CaO≤10.55％，0≤MgO≤4.0％，0≤SiO2≤11.33％，0≤Al2O3≤4.22％，Cl≤0.1％，Na+K≤0.65％。

【技术特征摘要】
1.一种改善喷吹用煤粉流动性的添加剂，其特征在于，所述添加剂为冶金除尘灰，所述冶金除尘灰组分及重量百分比如下：40％≤TFe≤62％，0≤C≤30％，0≤CaO≤10.55％，0≤MgO≤4.0％，0≤SiO2≤11.33％，0≤Al2O3≤4.22％，Cl≤0.1％，Na+K≤0.65％。2.如权利要求1所述的改善喷吹用煤粉流动性的添加剂，其特征在于：所述除尘灰添加质量分数≤20％。3.如权利要求1所述的改善喷吹用煤粉流动性的添加剂，其特征在于：所述冶金除尘灰的物理性质为500m2/kg≤比表面积≤2000m2/kg，400kg/m3≤自然堆积密度≤1000kg/m3，-74μm粒度组成≥90wt％，中位粒径D50≤15μm，粒度分布离散度1.0≤η≤5.0。4.如权...

【专利技术属性】
技术研发人员：高强健，沈峰满，王婉露，郑海燕，姜鑫，崔军坡，
申请(专利权)人：东北大学，
类型：发明
国别省市：辽宁,21