Super heat resistant epoxy resin composite coating and preparation method thereof

The invention relates to an ultra-heat-resistant epoxy resin composite coating and a preparation method thereof, belonging to the technical field of epoxy resin. The technical problem of the poor heat resistance of the epoxy resin in the prior art is solved. The composite coating of the invention is composed of 100 parts epoxy resin, 30 40 parts epoxy resin curing agent, 3 8 parts epoxy resin accelerator, 5 15 parts plasticizer, 10 25 parts diluent, 4 8 parts boron nitride, 5 7 parts carbon fiber and 3 5 parts nanometer titanium nitride. The coating has the characteristics of good adhesion, excellent mechanical properties and excellent heat resistance. The test results show that the coating has no foaming and no peeling after placed at 180 C for 5 hours.

【技术实现步骤摘要】
超耐热环氧树脂复合涂料及其制备方法
本专利技术属于环氧树脂
，具体涉及一种超耐热环氧树脂复合涂料及其制备方法。
技术介绍
环氧树脂具有粘结性好、固化收缩小、电性能好、化学稳定性好、容易改性等优异性能，用途广泛，尤其是涂料领域，广泛用作防锈底漆、地坪漆、工业重防腐漆、饮用水箱漆、油罐漆等。但是，由于固化后环氧树脂交联密度高，造成内应力大、质脆，以及耐热性差、摩擦系数高等不足而限制了环氧树脂的进一步应用。
技术实现思路
有鉴于此，为解决现有技术中环氧树脂耐热性差的技术问题，本专利技术提供一种超耐热环氧树脂复合涂料及其制备方法。本专利技术解决上述技术问题采取的技术方案如下。超耐热环氧树脂复合涂料，组成为：优选的，所述的环氧树脂为双酚A环氧树脂、酚醛环氧树脂、双酚F环氧树脂中一种或几种按任意配比混合。优选的，所述的环氧树脂固化剂为酸酐类固化剂、脂肪族胺类固化剂、芳香胺类固化剂中一种或几种按任意配比混合。优选的，所述环氧树脂促进剂为脂肪胺促进剂、酸酐促进剂、聚醚胺促进剂中一种或几种按任意配比混合。优选的，所述增塑剂为C5石油树脂、松香、增塑剂A、芳烃油或环烷油中的一种或多种。优选的，所述稀释本文档来自技高网...

【技术保护点】
1.超耐热环氧树脂复合涂料，其特征在于，组成为：

【技术特征摘要】
1.超耐热环氧树脂复合涂料，其特征在于，组成为：2.根据权利要求1所述的超耐热环氧树脂复合涂料，其特征在于，所述的环氧树脂为双酚A环氧树脂、酚醛环氧树脂、双酚F环氧树脂中一种或几种按任意配比混合。3.根据权利要求1所述的超耐热环氧树脂复合涂料，其特征在于，所述的环氧树脂固化剂为酸酐类固化剂、脂肪族胺类固化剂、芳香胺类固化剂中一种或几种按任意配比混合。4.根据权利要求1所述的超耐热环氧树脂复合涂料，其特征在于，所述环氧树脂促进剂为脂肪胺促进剂、酸酐促进剂、聚醚胺促进剂中一种或几种按任意配比混合。5.根据权利要求1所...

【专利技术属性】
技术研发人员：李英霞，
申请(专利权)人：长春智享优创科技咨询有限公司，
类型：发明
国别省市：吉林,22