The invention discloses a cable insulating layer with flame retardancy and a preparation method thereof. The preparation method includes: 1) mixing silica gel, carbon powder, cyclodextrin and water to produce a mixed solution; 2) hydrothermal reaction of the mixed solution, aluminum salt, magnesium salt and alkaline compound, and then filtering and drying to produce a flame retardant. 3) Natural rubber, polyvinyl chloride, hexabromocyclododecane, hydroxymethyl starch, talc powder, nano-titanium dioxide, silicone oil, sulfur and the flame retardant are mixed and shaped to produce cable insulation layer. The insulating layer of the cable has excellent flame retardancy, and the preparation method has the advantages of simple process and easy availability of raw materials.
【技术实现步骤摘要】
具有阻燃性的电缆绝缘层及其制备方法
本专利技术涉及阻燃剂，具体地，涉及一种具有阻燃性的电缆绝缘层及其制备方法。
技术介绍
电缆的缓冲层大多由橡胶组成，现有的橡胶缓冲层仅仅能够起到缓冲作用，在意外起火的情况下，橡胶则会在高温下分解为可燃性低分子物质。可燃性低分子物质则会讯速地与氧气进行剧烈的氧化反应，氧化反应放出大量的热则会进一步促进橡胶的分解，同时氧化反应中的生成物如低分子醇、醛也会与氧气进行氧化反应直至橡胶烧尽。
技术实现思路
本专利技术的目的是提供一种具有阻燃性的电缆绝缘层及其制备方法，该电缆绝缘层具有优异的阻燃性能，同时该制备方法具有工序简单和原料易得的优点。为了实现上述目的，本专利技术提供了一种具有阻燃性的电缆绝缘层的制备方法，包括：1)将硅胶、碳粉、环糊精和水进行混合以制得混合溶液；2)将混合溶液、铝盐、镁盐和碱性化合物进行水热反应，然后过滤、干燥以制得阻燃剂；3)将天然橡胶、聚氯乙烯、六溴环十二烷、羟甲基淀粉、滑石粉、纳米二氧化钛、硅油、硫磺和所述阻燃剂混炼、成型以制得电缆绝缘层。本专利技术还提供了一种具有阻燃性的电缆绝缘层，该于电缆绝缘层的阻燃剂通过上述...
【技术保护点】
1.一种具有阻燃性的电缆绝缘层的制备方法，其特征在于，包括：1)将硅胶、碳粉、环糊精和水进行混合以制得混合溶液；2)将所述混合溶液、铝盐、镁盐和碱性化合物进行水热反应，然后过滤、干燥以制得阻燃剂；3)将天然橡胶、聚氯乙烯、六溴环十二烷、羟甲基淀粉、滑石粉、纳米二氧化钛、硅油、硫磺和所述阻燃剂混炼、成型以制得电缆绝缘层。
【技术特征摘要】
1.一种具有阻燃性的电缆绝缘层的制备方法，其特征在于，包括：1)将硅胶、碳粉、环糊精和水进行混合以制得混合溶液；2)将所述混合溶液、铝盐、镁盐和碱性化合物进行水热反应，然后过滤、干燥以制得阻燃剂；3)将天然橡胶、聚氯乙烯、六溴环十二烷、羟甲基淀粉、滑石粉、纳米二氧化钛、硅油、硫磺和所述阻燃剂混炼、成型以制得电缆绝缘层。2.根据权利要求1所述的制备方法，其中，在步骤1)中，所述硅胶、碳粉、环糊精和水的重量比为40：5-10：15-20：200-400。3.根据权利要求1所述的制备方法，其中，在步骤1)中，所述混合满足以下条件：混合温度为40-60℃，混合时间为40-60min。4.根据权利要求1所述的制备方法，其中，在步骤2)中，所述混合溶液、铝盐、镁盐和碱性化合物的重量比为100：15-20：3-8：30-40。5.根据权利要求1所述的制备方法，其中，在步骤2)中，所述水热反应的条件为：反应温度为150-200℃，反应时间为6-10h。6.根...
【专利技术属性】
技术研发人员：章新能，佘晨，徐慧，芮永梅，
申请(专利权)人：芜湖航天特种电缆厂股份有限公司，
类型：发明
国别省市：安徽,34