The invention relates to a shoulder pad formulation for all steel engineering radial tire used in mines, which is characterized in that the components of the compound include natural rubber, styrene-butadiene rubber, carbon black, silica, zinc oxide, stearic acid, antioxidant 4020, antioxidant RD, post-vulcanization stabilizer HTS, N_tert-butyl_2_benzothiazole sulfonamide, and so on. Curing agent DTDM, anti-reversion agent PERKALINK 900, environment-friendly aromatic hydrocarbon oil and insoluble sulfur, etc., the rolled compound has good heat resistance, excellent aging resistance and excellent anti-reversion performance, and the service life of the tire made from this compound is prolonged.
【技术实现步骤摘要】
一种矿山用全钢工程子午线轮胎胎肩垫胶配方
本专利技术涉及一种矿山用全钢工程子午线轮胎胎肩垫胶配方，主要用于30.00R51、40.00R57等全钢工程子午线轮胎的胎肩垫胶胶料。
技术介绍
1946年法国米其林公司专利技术了子午线轮胎，为轮胎业带来了革命性的变化。其后又将这项技术推广到各类轮胎中，并于1959年制造出世界第一条子午线轮胎。子午线轮胎的问世，与斜交胎相比显示出了无比的优越性。因此，在西欧子午线轮胎发展得最早，发展速度也最快。早在1972年法国已经几乎100%子午化，到1989年末西欧轮胎市场已经100%子午化。全钢工程子午线轮胎具有节油、低生热、行驶里程高、负荷能力大、耐磨性能好、耐切割、耐刺扎、行驶安全舒适等性能，与斜交胎相比优势十分明显。在煤矿和铁矿中实际行驶里程和使用寿命为斜交胎的1.5-3倍，且经济效益显著，深受用户的欢迎。近年来世界各国对煤矿、铜矿、铁矿的巨额需求拉动了采掘业对采掘机械及大型运输车辆的需求，从而引起全钢工程子午线轮胎供不应求，其短缺程度比较严重。特别是30.00R51、33.00R51、36.00R51、40.00R57等规格...
【技术保护点】
1.一种矿山用全钢工程子午线轮胎胎肩垫胶配方，其特征是其胶料的各组分的重量比如下：天然橡胶 60‑100；丁苯橡胶 0‑40；氧化锌 3‑10；硬脂酸 1‑4；炭黑 ...
【技术特征摘要】
1.一种矿山用全钢工程子午线轮胎胎肩垫胶配方，其特征是其胶料的各组分的重量比如下：天然橡胶60-100；丁苯橡胶0-40；氧化锌3-10；硬脂酸1-4；炭黑40-50；白炭黑4-20；后硫化稳定剂HTS0.5-3；防...
【专利技术属性】
技术研发人员：王礼均，丁树强，张晨光，
申请(专利权)人：天津国际联合轮胎橡胶股份有限公司，
类型：发明
国别省市：天津,12
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。