The invention provides a matt heat-resistant ABS material, which comprises the following mass fractions: ABS resin 550 750 phr, heat-resistant agent 100 250 phr, toughener 100 200 phr, PE resin 10 30 phr, filler 10 30 phr, coupling agent 1 3 phr, antioxidant 2 5 phr, lubricant 2 5 phr. PE resin, coupling agent and filler were mixed in high-speed mixer, then ABS resin, toughening agent, heat-resistant agent, antioxidant and lubricant were added to continue to be uniform, and then the mixture was fed into twin-screw extruder to make granules. The Matt heat-resistant ABS material provided by the invention has the characteristics of low gloss, high heat-resistance and high impact, and is very suitable for products with low gloss requirements such as automotive interior accessories.
【技术实现步骤摘要】
一种亚光的耐热ABS材料及其制备方法
：本专利技术涉及高分子材料加工领域，具体地说涉及一种亚光的耐热ABS材料及其制备方法。
技术介绍
：ABS是一种高强度、高韧性的热塑性工程塑料，具有高光泽、易着色的特点，因此被广泛的用于家电、玩具、电子电器等领域，也广泛的应用于汽车内外饰件。在汽车内饰件的要求中，为避免制件表面光泽反射光线影响驾驶员视线，需要使用低光泽ABS，目前市场上存在的非高光ABS仍无法满足要求，而常用的消光剂或消光母粒价格昂贵。针对以上问题，本专利技术提供了一种适合于汽车内饰件的亚光耐热ABS材料。
技术实现思路
：本专利技术针对现有的ABS材料的特点和市场需求，提供了一种亚光的耐热ABS材料，该材料具有低光泽、高耐热、高冲击的特点，非常适用于汽车行业。本专利技术使用的技术方案如下：ABS树脂550-750份耐热剂100-250份增韧剂100-200份PE树脂10-30份填料10-30份偶联剂1-3份抗氧剂2-5份润滑剂2-5份所用的ABS树脂为本体法生产的丙烯腈-丁二烯-苯乙烯共聚物。所用耐热剂为苯乙烯-N-苯基马来酰亚胺-马来酸酐共聚物(MSNIP)和...
【技术保护点】
1.一种亚光的耐热ABS材料，其特征在于，包含以下质量份：ABS 550‑750份，耐热剂 100‑250份，增韧剂 100‑200份，PE树脂 10‑30份，填料10‑30份，偶联剂 1‑3份，抗氧剂 2‑5份，润滑剂 2‑5份。
【技术特征摘要】
1.一种亚光的耐热ABS材料，其特征在于，包含以下质量份：ABS550-750份，耐热剂100-250份，增韧剂100-200份，PE树脂10-30份，填料10-30份，偶联剂1-3份，抗氧剂2-5份，润滑剂2-5份。2.根据权利要求1所述的一种亚光的耐热ABS材料，其特征在于：所述的ABS树脂为本体法生产的丙烯腈-丁二烯-苯乙烯共聚物。3.根据权利要求1所述的一种亚光的耐热ABS材料，其特征在于：所述的耐热剂为苯乙烯-N-苯基马来酰亚胺-马来酸酐共聚物和苯乙烯-马来酸酐共聚物中的一种。4.根据权利要求1所述的一种亚光的耐热ABS材料，其特征在于：所述的增韧剂为ABS高胶粉或甲基丙烯酸酯-丁二烯-苯乙烯中的一种。5.根据权利要求1所述的一种亚光的耐热ABS材料，其特征在于：所述的PE为重均分子量在30-60万的高密度聚乙烯。6.根据权利要求1所述的一...