The invention relates to an interpenetrating network embolization microsphere and a preparation method thereof, which belongs to the field of medical technology. The invention discloses an interpenetrating network embolization microsphere, which is formed by crosslinking polyvinyl alcohol or gelatin with polymer monomer by using microfluidic technology and using oil-water microfluidic droplets as template. The microspheres were constructed. Thus, the composite polymer microspheres with good biocompatibility, flexibility and elasticity were obtained, which could be used in drug loading and anti-tumor embolic agents and other biomedical fields.
【技术实现步骤摘要】
互穿网络栓塞微球及其制备方法
本专利技术涉及互穿网络栓塞微球及其制备方法，属于医药
，特别是涉及微球型栓塞剂领域。
技术介绍
栓塞治疗，作为介入疗法的重要组成部分，因其在治疗恶性肿瘤、子宫肌瘤、血管畸形等方面取得的良好疗效，正得到越来越广泛的应用。一般地，栓塞治疗是在医学影像设备的引导下，将栓塞剂通过特制的导管、导丝等精密器械引入人体，阻塞靶区的血供和营养，以达到靶区肿瘤细胞缺血坏死的目的。栓塞治疗的关键在于选择合适的用于阻断肿瘤组织供血的颗粒栓塞剂。石蜡和凡士林混合颗粒、桂球、氰丙烯酸盐、无水乙醇、明胶海绵、碘酒、不锈钢圈、纤维胶、凝血酶与纤维蛋白形成的粘附混合物颗粒作为栓塞剂相继出现并应用于临床，但这些栓塞剂通常难以操控，且会带来严重副作用。微球型栓塞剂作为一种新型的颗粒栓塞剂，由于其具有形状统一、表面光滑，且亲水性、悬浮性好，易于随血流导向等优点得到越来越多的重视。现有微球按所用材料可分为聚乙烯醇微球、淀粉微球、白蛋白微球、聚乳酸微球、壳聚糖微球以及乙基纤维素微球等。但这些微球类栓塞剂的制备工艺复杂，难以大批量生产。此外，部分微球力学性能较差，不能承受...
【技术保护点】
1.互穿网络栓塞微球，其特征是，该微球是利用微流控技术，以油包水微流控液滴为模板，进行高分子单体以及聚乙烯醇或者明胶的分步化学交联形成的具有互穿网络结构的微球。
【技术特征摘要】
1.互穿网络栓塞微球，其特征是，该微球是利用微流控技术，以油包水微流控液滴为模板，进行高分子单体以及聚乙烯醇或者明胶的分步化学交联形成的具有互穿网络结构的微球。2.根据权利要求1所述互穿网络栓塞微球，其特征是，所述的高分子单体选自丙烯酰胺、甲基丙烯酰胺、N-甲基-2-丙烯酰胺、N-[三(羟甲基)甲基]丙烯酰胺中的任意一种或者上述两种或多种的混合物。3.权利要求1或2所述的互穿网络栓塞微球的制备方法，其特征是，包括以下步骤：（1）在氮气气氛下，将聚乙烯醇或者明胶溶解于去离子水或者去离子水与甘油的混合溶剂中得到水相溶液，然后将高分子单体加入水相溶液中，同时加入水溶性引发剂；（2）将油酸山梨坦作为乳化剂溶解于油相中，同时加入四甲基乙二胺；（3）采用可生成连续液滴的微流控芯片，以油相溶液为连续相，水相溶液为非连续相，生成油包水液滴，收集；（4）将步骤（3）得到的油包水液滴在20-40℃的条件下，静置，高分子单体交联形成交联网络，聚乙烯醇或明胶分子穿插在交联网络中；（5）高分子单体交联完成后，除去油相，将微球分散于丁醛、乙二醛、硼酸、戊二醛、或者谷氨酰胺转氨酶的水溶液中，在30-50℃的条件下继续反应，聚乙烯醇或明胶分子与高分子单体之间发生交联，形成互穿网络的高分子微球。4.根据权利要求3所述的互穿网络栓塞微球的制备方法，其特征是，步骤（1）中优选以下任意一个或者多个条件，聚乙烯醇或者明胶在水相溶液中的质...
【专利技术属性】
技术研发人员：张静，周进，陈捷，沈宇，
申请(专利权)人：南京慧联生物科技有限公司，
类型：发明
国别省市：江苏,32