The invention relates to a method for recovering lead from sponge lead, which belongs to the field of lead recovery technology. The sponge lead was dehydrated under the conditions of vacuum 0.03-0.07 MPa, vacuum melting dehydration temperature 350-400 C stirring, and the dehydration products of the upper layer as electrolyte and the lower layer as crude lead melt were obtained. Refined lead is obtained. The invention adopts vacuum smelting dehydration, and in the process of vacuum smelting dehydration, the electrolyte and the crude lead melt can be separated, the upper layer is the electrolyte, and the lower layer is the crude lead melt.
【技术实现步骤摘要】
一种从海绵铅中回收铅的方法
本专利技术涉及一种从海绵铅中回收铅的方法，属于铅回收
技术介绍
铅在工业领域应用广泛，在电气领域可用作蓄电池、电缆保护皮或熔断保险丝；在冶炼和化工领域，铅板或铅管可用作耐酸称里、防腐盖、原子能工业和光的防护层；此外，铅的化合物还能用于颜料工业、玻璃工业、石油工业及医药部门等。因此，铅的冶炼生产也得到广泛重视。湿法炼铅是精矿经浸出和电解产出金属铅的过程，在这一过程中，阴极板会得到含有大量水分、电解质和铜杂质，且质地疏松的海绵铅，若要从海绵铅中回收铅，需要去除其中的水分、电解质和铜杂质。传统海绵铅处理方式是由人工将阴极板上的海绵铅剥离脱落，然后放置于压力机的模具内，经压力机压制成块后，再干燥除水，最后送到精炼炉进行冶炼；后来王振云等人专利技术了自动从阴极板剥离海绵铅的装置，实现了机械剥离，生产效率有了一定程度的提升，但所采用的压制脱水的工序，脱水时间长，如将含水量为8%的海绵铅脱水至不含水，处理能力最大为0.2吨/h，影响了海绵铅回收铅的效率。
技术实现思路
针对上述现有技术存在的问题及不足，本专利技术提供一种从海绵铅中回收铅的方法。...
【技术保护点】
1.一种从海绵铅中回收铅的方法，其特征在于具体步骤包括：步骤1、将海绵铅在真空度为0.03~0.07MPa，真空熔炼脱水的温度为350~400℃搅拌条件下脱水，得到上层为电解质、下层为粗铅熔体的脱水产物，脱水产物经分层分离后得到粗铅熔体；真空熔炼脱水的时间为25~35min/吨；步骤2、将步骤1得到的粗铅熔体进行精炼，得到精铅。
【技术特征摘要】
1.一种从海绵铅中回收铅的方法，其特征在于具体步骤包括：步骤1、将海绵铅在真空度为0.03~0.07MPa，真空熔炼脱水的温度为350~400℃搅拌条件下脱水，得到上层为电解质、下层为粗铅熔体的脱水产物，脱水产物经分层分离后得到粗铅熔体；真空熔炼脱水的时间为25~35min/吨；步骤2、将步骤1得到的粗铅熔体进行精炼，得到精铅。2.根据权利要求1所述的从海绵铅中回收铅的方法，其特征在于：所述步骤1中海绵铅含水率为3~10wt%。3.根据权利要求1所述的从海绵铅中回收铅的方法，其特征在于：所述步骤1搅拌条件下脱水搅拌速度为50~80r/min。4.根据权利要求1所述的从海绵铅中回收铅的方法，其特征在于：所述步骤1中真空熔炼脱水得到的水蒸气将进行冷凝得到冷凝水。5.根据权利要求1所述的从海绵铅中回收铅的方法，其特征在于：所述步骤2精炼过程为在结晶分离装置中进行结晶分离精炼。6.根据权利要求5所述的从海绵铅...
【专利技术属性】
技术研发人员：蒋文龙，杨斌，梅青松，刘大春，徐宝强，李一夫，田阳，杨佳，查国正，郭新宇，邓聚海，张永伟，黄大鑫，邓勇，熊恒，王飞，
申请(专利权)人：昆明理工大学，
类型：发明
国别省市：云南,53