The invention relates to the field of automobile production technology, in particular to a processing method for enhancing the strength of boron steel automobile body and parts by laser quenching, which comprises a CO2 laser device or a semiconductor laser device or an optical fiber laser device, and is characterized by the following steps: adjusting the distance between the laser output lens and the boron steel plate Adjust the size of the spot; adjust the power of the laser; adjust the scanning speed of the laser; start the laser to scan the spot on the surface of the boron plate according to the predetermined route; cool the boron plate by air cooling, solid cooling or water cooling after the scanning.
【技术实现步骤摘要】
通过激光淬火提升硼钢汽车车身及部件强度的加工方法
本专利技术涉及汽车生产工艺领域，具体是一种通过激光淬火提升硼钢汽车车身及部件强度的加工方法。
技术介绍
汽车结构件需要高强度材料以满足保证使用性能下的轻量化条件。目前多采用热成形超高强度钢或激光焊接高强钢来实现该目的。但是，热成形后的零件会带来后续加工不便的问题；而激光焊接目前国际上还不能焊接1000MPa以上强度的超强钢。本项目旨在通过激光淬火工艺，对零部件需要满足强度要求的局部进行强化处理，实现零部件的局部高性能，从而走出另一条减轻车身重量的路线。激光淬火（也称激光强化）是一种近年来新兴的加工工艺，其作用原理是利用聚焦后的高能量密度大的激光束按序扫描钢铁材料表面，光能迅速转变成热能使材料被扫描范围快速升温并在停止扫描后快速冷却，从而使被加工表层材料产生相变硬化，进而达到提升材料表面性能的目的。目前，激光淬火作为高新技术而应用于航空航天、重工等领域，例如，申请号为201710277867.5的专利技术专利申请公开了一种将激光淬火应用于一次性航空材料上的加工方法，通过该篇申请文件可以知晓，钢材通过不同工艺参数的激光...
【技术保护点】
1.一种通过激光淬火提升硼钢汽车车身及部件强度的加工方法，其包括一台功率调节范围在0~5kw的CO2激光发射器或半导体激光设备或光纤激光设备，其特征是：还包括下述步骤：步骤1、将硼钢板材用夹具固定；步骤2、调整激光输出镜头使其与硼钢板材之间的距离为100mm~200mm、照射光斑的尺寸为10mm*2mm ~20mm*3mm ； 步骤3、调整激光器使其功率在1200w~4000w；步骤4、调整激光器使其扫描速度为1200mm/min~300mm/min；步骤5、启动激光器，使光斑以蛇形行进或直线行进的方式按预定路线在硼钢板材表面进行扫描；步骤6、待扫描完成后以空冷、固冷或水冷...
【技术特征摘要】
1.一种通过激光淬火提升硼钢汽车车身及部件强度的加工方法，其包括一台功率调节范围在0~5kw的CO2激光发射器或半导体激光设备或光纤激光设备，其特征是：还包括下述步骤：步骤1、将硼钢板材用夹具固定；步骤2、调整激光输出镜头使其与硼钢板材之间的距离为100mm~200mm、照射光斑的尺寸为10mm*2mm~20mm*3mm；步骤3、调整激光器使其功率在1200w~4000w；步骤4、调整激光器使其扫描速度为1200mm/min~300mm/min；步骤5、启动激光器，使光斑以蛇形行进或直线行进的方式按预定路线在硼钢板材表面进行扫描；步骤6、待扫...