一种环氧树脂粘结材料制造技术

本发明专利技术公开一种环氧树脂粘结材料。本发明专利技术组分包括环氧树脂、增韧剂、填料、偶联剂、添加剂、聚硫醇、聚酰胺、填料、颜料等原料。本发明专利技术采用添加剂海藻酸钠加入到环氧粘胶中，当这种环氧胶粘结的树脂板与钢工件板需要在常温水中浸泡时，由于添加剂海藻酸钠能吸收大量水分使环氧粘胶失效，因而树脂板与钢工件板在常温水中能容易分开。本发明专利技术材料环保，对工作人员的伤害极大的降低；相比于现有技术，能实现在常温水下快速使环氧粘胶失效。

An epoxy resin adhesive material

The invention discloses an epoxy resin bonding material. The components of the invention include epoxy resin, toughening agent, filler, coupling agent, additive, polymercaptan, polyamide, filler, pigment and other raw materials. The additive sodium alginate is added into the epoxy viscose. When the epoxy bonded resin board and the steel workpiece board need to be immersed in normal temperature water, the epoxy viscose is invalid because the additive sodium alginate can absorb a large amount of water, so the resin board and the steel workpiece board can be easily separated in normal temperature water. The material of the invention is environmentally friendly, and the injury to the staff is greatly reduced; compared with the existing technology, the epoxy adhesive can be quickly invalidated under normal temperature.

【技术实现步骤摘要】
一种环氧树脂粘结材料
本专利技术属于材料制备
，涉及高分子粘结材料的制备，具体是一种环氧树脂粘结材料。
技术介绍
太阳能光伏发电一般指能利用半导体直接将光能转换为电能的一种能源形式。光伏能源具有无污染、无噪声、维护成本低、使用寿命长等优点，近年来得到了飞速发展。以硅片构建的晶硅类太阳能电池是光伏发电最普遍的一种形式，在硅片切割生产过程中必须使用硅棒胶粘结固定硅棒与树脂板，同时使用水煮胶粘结树脂板与钢工件板。这种水煮胶粘结的树脂板与钢工件板在热水中能脱胶，使钢工件板能够反复使用。由于环氧树脂粘胶具有粘接强度高、通用性强和价格相对低廉等特点，并且电绝缘性优良、化学性能稳定及加工性能良好等一系列优异性能，因此硅片切割水煮胶目前主要采用双组份环氧树脂粘胶。常州大学陶宇等公开了一种硅棒切割用环氧环氧胶及制备方法专利技术专利(申请号：201210258425.3)，在环氧树脂胶中采用了碳酸氢铵、碳酸氢钠、连二亚硫酸钠或磷酸氢钙等粉末无机盐作为脱胶剂，在水中50～60℃下分解反应产生气体，从而使这种环氧胶粘结的树脂板与钢工件板在热水中能脱胶。但这些无机盐在热水中分解产生的气量小，因此脱胶时间本文档来自技高网...

【技术保护点】
1.一种环氧树脂粘结材料，由A、B双组分组成，其特征在于其组分所含原料和配比如下：

【技术特征摘要】
1.一种环氧树脂粘结材料，由A、B双组分组成，其特征在于其组分所含原料和配比如下：所述的环氧树脂为双酚A环氧树脂、双酚F环氧树脂的一种或二种混合；所述的增韧剂为氯代甲氧基脂肪酸甲酯；所述的填料为碳酸钙、二氧化硅、氧化...

【专利技术属性】
技术研发人员：聂秋林，
申请(专利权)人：杭州电子科技大学，
类型：发明
国别省市：浙江,33