The invention relates to a PS foaming material and a preparation method thereof, in which 80 parts of PS, 10 parts of Ag/PS and 0.1 parts of antioxidant are mixed and stirred evenly to obtain a mixture; the obtained mixture is put into a twin-screw extruder to extrude and granulate; the obtained granular material is placed in a high-pressure kettle and passed into supercritical two. Carbon oxide, heated to melting state, adjusting the pressure in 20 24 MPa, reaction 8 10 h after the pressure drop PS foaming material. Ag + in this application has heterogeneous nucleation effect, it can significantly improve the nucleation efficiency, compared with ordinary PS foam, PS foam pore density in this application is larger; heterogeneous nucleation reduces the bubble diameter, compared with ordinary PS foam, PS foam in this application has better mechanical properties.
【技术实现步骤摘要】
一种PS发泡材料及其制备方法
本专利技术属于高分子材料
，特别是指一种PS发泡材料及其制备方法。
技术介绍
聚苯乙烯(PS)发泡是一种重要的发泡材料，广泛应用于家用电器、机械配件、办公用品和通讯器材等领域。PS发泡具有质轻、无毒、无臭，吸水性好等优点，但是普通PS发泡的物理性能一般，这限制了PS发泡在一些
上的应用。本技术方案创新的制得了一种PS发泡材料，它具有很好的物理性能，这种材料至今尚未见于报道，这对于扩展PS发泡复合材料的应用具有非常重要的现实意义。
技术实现思路
本专利技术的目的是提供一种PS发泡材料及其制备方法，以解决现有技术的PS发泡的物理性能无法满足有些特定方面的内容。本专利技术是通过以下技术方案实现的：一种PS发泡材料，按重量份由以下组分组成：所述Ag/PS粒子的制备方法，包括以下步骤：(1)称取一定量的聚苯乙烯、1-甲基-2-吡咯烷酮、硝酸银溶液、二甲基乙酰胺及乙醇溶液；(2)将聚苯乙烯、1-甲基-2-吡咯烷酮、硝酸银溶液、二甲基乙酰胺及乙醇溶液放入三口烧瓶中，在80-100℃的油浴环境下反应4-6h，在放入冷水中冷却1-2h，得到Ag...
【技术保护点】
1.一种PS发泡材料，其特征在于，按重量份由以下组分组成：
【技术特征摘要】
1.一种PS发泡材料，其特征在于，按重量份由以下组分组成：2.根据权利要求1所述的PS发泡材料，其特征在于，所述Ag/PS粒子的制备方法，包括以下步骤：(1)称取一定量的聚苯乙烯、1-甲基-2-吡咯烷酮、硝酸银溶液、二甲基乙酰胺及乙醇溶液；(2)将聚苯乙烯、1-甲基-2-吡咯烷酮、硝酸银溶液、二甲基乙酰胺及乙醇溶液放入三口烧瓶中，在80-100℃的油浴环境下反应4-6h，在放入冷水中冷却1-2h，得到Ag/PS溶胶；(3)将Ag/PS溶胶进行过滤、洗涤、干燥，得到Ag/PS粒子。3.根据权利要求2所述的PS发泡材料，其特征在于，步骤(1)中的聚苯乙烯、1-甲基-2-吡咯烷酮、硝酸银溶液、二甲基乙酰胺及乙醇溶液的质量比是(40-60)：(0.1-0.3)：(30-50)：(10-30)：(180-240)。4.根据权利要求1所述的PS发泡材料，其特征在于，所述发泡剂为超临界CO2。5.根据权利要求1所述的PS发泡材料，其特征在于，所述抗氧剂为三(2,4-二叔丁基)亚磷酸苯酯、四[β-(3，5...
【专利技术属性】
技术研发人员：刘凯，伏建博，贾丙林，
申请(专利权)人：安徽江淮汽车集团股份有限公司，
类型：发明
国别省市：安徽,34