The invention discloses an organic-inorganic hybrid perovskite nanometer material and a preparation method thereof, including: dispersing piperazine and BX in water, obtaining a mixed solution, adding HX into the mixed solution, obtaining an acidic mixed solution; putting the acidic mixed solution for 3 days 7 days, appearing colorless massive crystals, and being a massive organic-inorganic hybrid perovskite C4H12. N2BX3.H2O; the bulk organic-inorganic hybrid perovskite C4H12N2BX3.H2O was heated at 100 120 The invention provides a method for preparing organic-inorganic hybrid perovskite nano-materials in large quantities and at low cost. The hybrid perovskite nano-materials prepared by the method have the advantages of simple process, low cost, mild reaction conditions and safety without high temperature and high pressure reaction.
【技术实现步骤摘要】
一种有机无机杂化钙钛矿纳米材料及其制备方法
本专利技术属于纳米材料制备领域，更具体地，涉及一种有机无机杂化钙钛矿纳米材料及其制备方法。
技术介绍
“钙钛矿”一词现在指的是一大类具有同CaTiO3结构相同的材料，即钙钛矿结构。钙钛矿材料的一般化学式为ABX3形式，A和B是不同大小的阳离子，X是与B配位的阴离子，通常情况下A位阳离子半径大于B位阳离子半径，并且B位与X位阴离子六配位形成一个BX6的八面体。这些八面体通过顶点共享形成一个三维框架，A位阳离子位于框架中心。杂化有机无机钙钛矿(HOIP)是ABX3材料的子类，其中A位和B位的离子分别被有机胺阳离子和有机桥接配体或卤素原子代替.这些HOIP结构中的有机组分引入了额外的功能和结构灵活性，这在纯无机钙钛矿中是无法实现的。最重要的是，它们不同的结构和化学的多样性为通过简单的化学修饰调整和调节其物理性质提供了大量机会。近年来，有机无机杂化钙钛矿材料由于其低廉的制造成本以及其独特的物理性质尤其是在光伏(PV)和光电子(OE)器件中的高性能而激发了科学界和工业界的广泛兴趣。由于钙钛矿纳米材料独特性能和应用引起人们的关注，制...
【技术保护点】
1.一种有机无机杂化钙钛矿纳米材料的制备方法，其特征在于，包括：(1)将哌嗪和BX分散在水中，得到混合液，向混合液中加入HX，得到酸性混合液；(2)将酸性混合液放置3天‑7天，出现无色块状晶体，为块状有机无机杂化钙钛矿C4H12N2BX3·H2O；(3)将块状有机无机杂化钙钛矿C4H12N2BX3·H2O在100℃‑120℃下加热1h‑3h，得到纳米尺度的杂化钙钛矿C4H12N2BX3；其中，B为K或Rb，X为Br、Cl或者I。
【技术特征摘要】
1.一种有机无机杂化钙钛矿纳米材料的制备方法，其特征在于，包括：(1)将哌嗪和BX分散在水中，得到混合液，向混合液中加入HX，得到酸性混合液；(2)将酸性混合液放置3天-7天，出现无色块状晶体，为块状有机无机杂化钙钛矿C4H12N2BX3·H2O；(3)将块状有机无机杂化钙钛矿C4H12N2BX3·H2O在100℃-120℃下加热1h-3h，得到纳米尺度的杂化钙钛矿C4H12N2BX3；其中，B为K或Rb，X为Br、Cl或者I。2.如权利要求1所述的一种有机无机杂化钙钛矿纳米材料的制备方法，其特征在于，所述哌嗪和BX的摩尔比为1∶1。3.如权利要求1或2所述的一种有机无机杂化钙钛矿纳米材料的制备方法，其特征在于，所述酸性混合液的PH值...
【专利技术属性】
技术研发人员：李伟，张亚楠，陆培祥，
申请(专利权)人：华中科技大学，
类型：发明
国别省市：湖北,42