The invention discloses a calcified ecological brick and a production method thereof. The calcified brick takes fine sand, hydrophilic fiber and calcium carbonate as main raw materials, and is cemented and formed by the method of microbial calcification. The composition of calcified brick is: fine sand 60 80, fiber 0.24 0.8, calcium carbonate 20 30, the rest is water. The fine sand used in the invention can save clay and other land resources, the product quality meets the standards, the production process is simple, the large-scale equipment is not needed, the fine sand can be produced in open air or factory prefabrication, and is a fast and energy-saving building material production mode.
【技术实现步骤摘要】
一种钙化生态砖及其生产方法
本专利技术涉及工程建设
，具体是一种钙化生态砖及其生产方法。
技术介绍
砖是一种古老的建筑材料，早在春秋战国时期我国就出现了制砖工艺。传统砖的工艺生产方法包括：烧结、蒸压、蒸养等。大部分建筑、道路用砖通过烧制而成，主要组成原料包括粘土和少量砂石。然而这类砖用土量大、资源浪费严重国家已逐渐禁止生产。近年来出现了以煤矸石、粉煤灰等工业废料为主的灰砂砖以及建筑废料为主的砌块等新型砖材。它们或通过蒸压养护制备或添加水泥、石膏等凝胶材料胶结而成。通过烧结或蒸养形成的砖需要煅烧炉或蒸压釜等大型工业设备，而添加胶凝材料生产的砖，砂石比例少，水泥和煤灰等凝胶活性材料需要量至少40％以上。这些制砖方法前期投入较高，需要上游材料供应，能源耗费较大常常采用工业化的生产方式来降低成本，仅适合人口稠密、经济发达的地区。随着基础设施建设的不断提速，开发利用远离城镇的荒地、沙漠等传统“不可利用土地资源”将逐渐成为发展趋势。缺少工业体系、工业原料给传统技术附加了高额的成本。充分使用当地已有砂石，更新砖这一基础建材的生产工艺对实现可持续发展优化生态环境具有重要的意...
【技术保护点】
1.一种钙化生态砖的生产方法，其特征在于，包括以下步骤:1)制备原料：1‑1)原料预处理除去原料中小于0.1mm的颗粒，并筛除大于0.5mm的颗粒。1‑2)按照以下配比称量原料：细砂60～80份纤维0.24～0.8份2)砖胚制作：根据设定的干密度按照含水量在0.6‑2.4份之间，加水拌合细砂和纤维，装入所述制胚模具，并压实至设定干密度，并用水充分润湿，得到砖胚；3)钙化胶结：3‑1)测定同一批次制作的砖胚的孔隙体积3‑2)配置含脲酶的细菌溶液或大豆脲酶溶液；3‑3)以自由渗透的方式向砖胚中加入含脲酶的吸光度OD600为0.6‑1.2之间细菌溶液或1‑3g/L的脲酶溶液，加入...
【技术特征摘要】
1.一种钙化生态砖的生产方法，其特征在于，包括以下步骤:1)制备原料：1-1)原料预处理除去原料中小于0.1mm的颗粒，并筛除大于0.5mm的颗粒。1-2)按照以下配比称量原料：细砂60～80份纤维0.24～0.8份2)砖胚制作：根据设定的干密度按照含水量在0.6-2.4份之间，加水拌合细砂和纤维，装入所述制胚模具，并压实至设定干密度，并用水充分润湿，得到砖胚；3)钙化胶结：3-1)测定同一批次制作的砖胚的孔隙体积3-2)配置含脲酶的细菌溶液或大豆脲酶溶液；3-3)以自由渗透的方式向砖胚中加入含脲酶的吸光度OD600为0.6-1.2之间细菌溶液或1-3g/L的脲酶溶液，加入溶液的量为砖胚孔隙体积的0.7-1倍，静置3-4小时；3-4...
【专利技术属性】
技术研发人员：肖杨，何想，刘汉龙，丁选民，肖鹏，汪杨，陈辉，王翔，
申请(专利权)人：重庆大学，
类型：发明
国别省市：重庆,50