The invention discloses a preparation method of graphite paper/manganese dioxide composite material, the steps are as follows: the graphite paper is cut into 2 *2 cm 2 square sheets, soaked in HCl, deionized water, KOH and deionized water with the concentration of 1 mol/L for 2 3 hours, then washed with deionized water, and connected with copper wire after treatment. The interface was sealed with epoxy resin and a blank graphite paper electrode was obtained. The graphite paper was used as working electrode and electrodeposited in the solution containing 0.10mol/L KCl and 0.10mol/L Mn (CH3COO) 2. The electrode was deposited at 1.5_1.7V constant voltage for 1.5_2.5min. The method is simple, easy to operate and fast. The electrode materials prepared by this method have good flexibility and can be widely used in flexible electronic products.
【技术实现步骤摘要】
一种石墨纸/二氧化锰复合材料的制备方法
本专利技术涉及一种石墨纸/二氧化锰复合材料的制备方法。
技术介绍
超级电容器作为新型的能量储存装置，比传统电池的储能量更大，具有循环寿命长，功率密度高，对环境无污染等特点，符合当今绿色环保理念，并且可以广泛用于军事和交通等诸多领域。超级电容器的电极材料主要为：碳材料、金属氧化物和聚合物等。其中，MnO2对环境无污染，而且理论上比电容较高，同时我国金属锰资源丰富，市场上价格低廉，是比较理想的超级电容器电极材料，但是由于其导电性差，在使用过程中常需要和导电性良好的碳材料复合。
技术实现思路
本专利技术的目的在于提供一种石墨纸/二氧化锰复合材料的制备方法。本专利技术通过下面技术方案实现：一种石墨纸/二氧化锰复合材料的制备方法，包括如下步骤：石墨纸切成2×2cm2的正方形小片，依次在浓度为1mol/L的HCl、去离子水、浓度为1mol/L的KOH和去离子水中浸泡2-3h，然后用去离子水冲洗干净，经处理后用铜线连接，接口处用环氧树脂密封，得到空白的石墨纸电极；以石墨纸为工作电极，在含有浓度为0.10mol/L份KCl和0.10mol/L的...
【技术保护点】
1.一种石墨纸/二氧化锰复合材料的制备方法，其特征在于包括如下步骤：石墨纸切成2×2cm2的正方形小片，依次在浓度为1mol/L的HCl、去离子水、浓度为1mol/L的KOH和去离子水中浸泡2‑3h，然后用去离子水冲洗干净，经处理后用铜线连接，接口处用环氧树脂密封，得到空白的石墨纸电极；以石墨纸为工作电极，在含有浓度为0.10mol/L份KCl和0.10mol/L的Mn(CH3COO)2的溶液中进行电沉积，在1.5‑1.7V恒电压下沉积1.5‑2.5min，即得。
【技术特征摘要】
1.一种石墨纸/二氧化锰复合材料的制备方法，其特征在于包括如下步骤：石墨纸切成2×2cm2的正方形小片，依次在浓度为1mol/L的HCl、去离子水、浓度为1mol/L的KOH和去离子水中浸泡2-3h，然后用去离子水冲洗干净，经处理后用铜线连接，接口处用环氧树脂密封，得到空白的石墨纸电极；以石墨纸为工作...
【专利技术属性】
技术研发人员：不公告发明人，
申请(专利权)人：启东创绿绿化工程有限公司，
类型：发明
国别省市：江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。