The invention discloses a mildew-proof processing method for bamboo used for furniture, which is treated by sugar removal, decolorization oxidation, neutralization and drying; sugar removal is carried out by alkali treatment; decolorization oxidation is carried out by hydrogen peroxide oxidation; neutralization is carried out by using Na2S2O4 with a concentration of 0.5% to neutralize residual hydrogen peroxide, and finally drying. The processing method of the invention also improves the appearance quality of the treated bamboo, improves the beauty of the bamboo products, and solves the problems of mildew and insect moth of the bamboo.
【技术实现步骤摘要】
家具用竹材的防霉处理方法
本专利技术涉及家具用的竹制品，尤其涉及家具用竹材的防霉处理方法。
技术介绍
自古以来人类就喜欢用木材和竹材来装点室内环境和制作室内家具。因此，实木家具和圆竹家具历史悠久，源远流长，直至现代仍为人们所喜爱。竹集成材家具是近几年开发出来的新生竹家具，因其材料具有大自然赋予的独特美感以及优越的材料特性，并具有生态性和环保性而为国内外，特别为环保意识较强的欧美发达国家所青睐。竹子具有繁殖容易，生长快，成材早，产量高，具有一次造林成功,可年年择伐，永续利用而不破坏生态环境的特点。由于竹材结构和化学组成都和木材有很大差异，其强度和密度都高于一般木材，竹材产品的强度大于一般木材产品,因此可用较小厚度的竹材产品替代较大厚度的木材产品，以取得经济上的优势。竹材纹理通直，质感爽滑，色泽简洁，易于漂白、染色和炭化等处理，完全可以和一些阔叶材相媲美，是生产集成材的优质材料。竹子主要是由纤维素、半纤维素、木质素、糖类等化学成分组成，这些都是蛀虫、细菌的好饲料，所以竹制家具易生虫、生霉，因此做为家具用的竹材，必须要经过三防处理，即防腐、防虫和防蛀。
技术实现思路
基于上述问题，本专利技术公开一种家具用竹材的防霉处理方法，方法简单，且不产生废水，所得竹材即防霉，同时也进行了漂白处理。本专利技术所采用的技术方案如下：家具用竹材的防霉处理方法，步骤1：除糖，采用碱处理法对竹材进行除糖处理，将竹材浸泡在浓度为1.25％NaOH溶液中，温度80-90℃，浸泡时间30分钟以上，不超过60分钟；步骤2：脱色氧化，用浓度为1-1.5％的过氧过氢，水温保持在60-70℃，PH值1...
【技术保护点】
1.家具用竹材的防霉处理方法，其特征在于：步骤1：除糖，采用碱处理法对竹材进行除糖处理，将竹材浸泡在浓度为1.25％NaOH溶液中，温度80‑90℃，浸泡时间30分钟以上，不超过60分钟；步骤2：脱色氧化，用浓度为1‑1.5％的过氧过氢，水温保持在60‑70℃，PH值10‑11，浸泡4‑6小时，浸泡过程中，加一次稳定剂；步骤3：中和，溶液采用浓度为0.5％的Na2S2O4，溶液的PH值5‑6，浸泡时间为5‑7小时；步骤4：烘干，烘干房温度为50‑70℃，烘3‑5小时。
【技术特征摘要】
1.家具用竹材的防霉处理方法，其特征在于：步骤1：除糖，采用碱处理法对竹材进行除糖处理，将竹材浸泡在浓度为1.25％NaOH溶液中，温度80-90℃，浸泡时间30分钟以上，不超过60分钟；步骤2：脱色氧化，用浓度为1-1.5％的过氧过氢，水温保持在60-70℃，PH值10-11，浸...
【专利技术属性】
技术研发人员：李家毅，
申请(专利权)人：海宁玖洲家具有限公司，
类型：发明
国别省市：浙江,33