The invention discloses an anti-aging interior wall coating, which relates to the coating field, including the following components: acrylic emulsion, acrylic acid, butyl acrylate, four butyl titanate, nano silica, nano manganese oxide, N hydroxyacrylamide, four methyl ammonium hydroxide methanol solution, acrylonitrile, fumed silica, and oxidation. Aluminum; Carboxyl monomer; Talc powder; Defoamer; Leveling agent; Dispersant; Stabilizer; Emulsifier; Thickener; Antioxidant; Pigment; Filler; Deionized water. The invention improves the ageing resistance of the exterior wall coating, solves the problem that adding nano-particles in the existing coatings can cause the heat preservation performance of the coatings to decline rapidly, and makes the comprehensive performance of the coatings more superior.
【技术实现步骤摘要】
一种抗老化的内墙用涂料
本专利技术涉及涂料领域，具体而言，涉及一种抗老化的内墙用涂料。
技术介绍
涂料主要涂于物体表面能形成具有保护、装饰或特殊性能(如绝缘、防腐、标志等)的固态涂膜的一类液体或固体材料的总称。近几年，国外建筑涂料无论从品种、规模应用、质量水平以及建筑涂料的研究水平上都有了很大的发展，使建筑涂料成为国外涂料中产量最大的一种。但购买涂料的合格与否直接影响到整体装修效果和居室的环境，有时甚至会对人体的健康产生极大的危害。目前随着各种各样涂料的产生，对涂料的品质要求也不断提高，而不断提高涂料质量对于建筑、生活都可以起到很大的帮助作用；但是大多数内墙漆还是存在涂层不坚固、附着力不强、涂层易脱落、耐洗刷性、耐酸碱性、耐污性不强、有害物大大超过国家限量标准等方面的不足，因此，生产一种高性能且无毒无害的内墙建筑漆实为人们所期盼。
技术实现思路
本专利技术的目的在于提供一种抗老化的内墙用涂料，以解决上述问题。为实现本专利技术目的，采用的技术方案为：一种抗老化的内墙用涂料，按重量份数计包括下列组份：丙烯酸乳液20-35份；丙烯酸15-25份；丙烯酸丁酯10-15份；钛酸...
【技术保护点】
1.一种抗老化的内墙用涂料 ，其特征在于，按重量份数计包括下列组份：丙烯酸乳液20‑35份；丙烯酸15‑25份；丙烯酸丁酯10‑15份；钛酸四丁酯20‑25份；纳米二氧化硅10‑20份；纳米氧化锰10‑15份； N‑羟基丙烯酰胺5‑15份；四甲基氢氧化铵甲醇溶液8‑12份；丙烯腈3‑7份；气相二氧化硅7‑12份；氧化铝5‑12份；羧基单体3‑5份；滑石粉5‑12份；消泡剂1‑5份；流平剂1.5‑4份；分散剂2‑8份；稳定剂2.5‑5份；乳化剂2‑5份；增稠剂2‑5份；抗氧化剂5‑8份；颜料0‑5份；填料10‑15份；去离子水10‑35份。
【技术特征摘要】
1.一种抗老化的内墙用涂料，其特征在于，按重量份数计包括下列组份：丙烯酸乳液20-35份；丙烯酸15-25份；丙烯酸丁酯10-15份；钛酸四丁酯20-25份；纳米二氧化硅10-20份；纳米氧化锰10-15份；N-羟基丙烯酰胺5-15份；四甲基氢氧化铵甲醇溶液8-12份；丙烯腈3-7份；气相二氧化硅7-12份；氧化铝5-12份；羧基单体3-5份；滑石粉5-12份；消泡剂1-5份；流平剂1.5-4份；分散剂2-8份；稳定剂2.5-5份；乳化剂2-5份；增稠剂2-5份；抗氧化剂5-8份；颜料0-5份；填料10-15份；去离子水10-35份。2.根据权利要求1所述的抗老化的内墙用涂料，其特征在于，所述羧基单体采用...