The invention discloses a heat insulation coating, which comprises the following raw materials in weight portion: 23 - 50, diatomite and sepiolite 30 - 60, 5 - 10 SiO2-TiO2 composite oxide, paraffin 2 - 5; first, during the preparation of SiO2-TiO2 composite oxides as wall material, paraffin /SiO2-TiO2 composite phase change microcapsules prepared by the sol-gel method, and then the /SiO2-TiO2 composite paraffin microcapsule with diatomite, sepiolite can be fully mixed. Insulation coating of the invention, the latent heat insulation performance over 80J/g, the effect is significant, and the thermal cycling test 500 and 1000 times in the stable performance, while addressing the paint dry easy to crack and peeling problems.
【技术实现步骤摘要】
本专利技术属于特种涂料材料领域，具体涉及保温涂料。
技术介绍
当今社会，建筑能耗占总能耗的比例越来越大，开展建筑节能具有十分重要的现实意义。保温涂料施涂于建筑物表面可有效地降低建筑物表面的温度，对于改善生活环境和节约能源效果明显。研究和开发建筑保温涂料具有重大的经济效益、环境效益和社会效益。在市场需求的推动下，保温节能类产品发展迅速，产品性能显著提高，但是仍旧存在一定的不足：1)保温效果差；2)涂料在长期使用过程中容易粉化、开裂甚至脱落。
技术实现思路
有鉴于此，本专利技术的目的是提供一种保温涂料，其特点是高温下呈微膨胀性、保温节能效果显著、性能稳定。为达到上述目的，本专利技术采用如下解决方案：本专利技术的保温涂料，它包含下列重量份的原料：硅藻土23—50份、海泡石绒30—60份、SiO2-TiO2复合氧化物5—10份、石蜡2—5份；制备时，首先SiO2-TiO2复合氧化物为壁材，利用溶胶凝胶法制备了石蜡/SiO2-TiO2复合相变微胶囊，然后再将石蜡/SiO2-TiO2复合相变微胶囊与硅藻土、海泡石绒充分混合即可。进一步，所述石蜡/SiO2-TiO2复合相变微胶囊的制各：将无水乙醇、正硅酸四乙酯混合搅拌反应，搅拌至形成溶胶；用盐酸将二次去离子水pH调制至2～3，将石蜡溶解于去离子水中，加入石蜡质量1％的十二烷基硫酸钠，超声震荡乳化，得到乳白色乳液；将乳液逐滴加入二氧化硅溶胶中，滴加完...
【技术保护点】
一种保温涂料，其特征在于，它包含下列重量份的原料：硅藻土23—50份、海泡石绒30—60份、SiO2‑TiO2复合氧化物5—10份、石蜡2—5份；制备时，首先SiO2‑TiO2复合氧化物为壁材，利用溶胶凝胶法制备了石蜡/SiO2‑TiO2复合相变微胶囊，然后再将石蜡/SiO2‑TiO2复合相变微胶囊与硅藻土、海泡石绒充分混合即可。
【技术特征摘要】
1.一种保温涂料，其特征在于，它包含下列重量份的原料：硅藻土23—50
份、海泡石绒30—60份、SiO2-TiO2复合氧化物5—10份、石蜡2—5份；制备
时，首先SiO2-TiO2复合氧化物为壁材，利用溶胶凝胶法制备了石蜡/SiO2-TiO2
复合相变微胶囊，然后再将石蜡/SiO2-TiO2复合相变微胶囊与硅藻土、海泡石
绒充分混合即可。
2.根据权利要求1所述的一种保温涂料，其特征在于：所述石蜡/SiO2-TiO2
复合相变微胶囊的制各：
将无水乙醇、正硅酸四乙酯混合搅拌反应，搅拌至形成溶胶；
用盐酸将二次去离子水pH调制至2～3，将石蜡溶解于去离子水...