The invention relates to the technical field of building materials, in particular to a ceramic tile adhesive and a preparation method thereof. The invention provides a ceramic tile adhesive, which comprises 30 40 portions of cement, 55 65 portions of inorganic porous material powder through 30 mesh sieve and 0.05 4 portions of optional additives. The use of inorganic porous material powder instead of traditional sand reduces the amount of sand, and the porous structure has a large specific surface area, thus reducing the density of ceramic tile adhesive, thereby reducing the weight bearing of the matrix. When the particle size of inorganic porous material powder is limited to less than 500 micron (through 30 mesh sieve), the composition of ceramic tile adhesive can be uniform without losing the advantage of inorganic porous material powder.
【技术实现步骤摘要】
瓷砖胶及其制备方法
本专利技术涉及建筑材料
，具体而言，涉及一种瓷砖胶及其制备方法。
技术介绍
随着社会的进步，瓷砖相关行业快速发展，瓷砖的种类和应用场景越来越多。一方面，传统的瓷砖粘贴方法多采用水泥砂浆，即将砂和水泥现场混合制成简单的水泥砂浆。把这种砂浆涂在预浸或者预润湿瓷砖背面，将涂有砂浆的瓷砖压到预先润湿的表面上，然后轻敲瓷砖，以保证瓷砖具有一致的平整度。这种砂浆的缺点为易泛碱、涂层厚、粘结力弱、耐久性差、容易剥落、施工材料用量大。另一方面，低吸水率且尺寸越来越大的瓷砖成为建筑施工的主流选择，由于瓷砖背面致密光滑，水泥浆无法渗透到瓷砖背面，易出现脱落问题，还必须机械固定或者加固。现有的瓷砖胶，要不断的进行改进才能满足质量上的要求。目前的瓷砖胶砂用量大，施工时用量大，同时密度高，导致墙体的承重过大并且容易出现脱落等问题。因此，开发一种密度小，粘结能力强，施工用量少的瓷砖胶具有重要的意义。有鉴于此，特提出本专利技术。
技术实现思路
本专利技术的目的在于提供一种瓷砖胶及其制备方法，以缓解现有技术的瓷砖胶中砂的使用量过大，密度过大并且施工用量大的技术问题。为了实现...
【技术保护点】
1.一种瓷砖胶，其特征在于，按重量份数计，包括以下原料：水泥30‑40份、过‑30目筛的无机多孔材料粉体55‑65份和任选的助剂0.05‑4份。
【技术特征摘要】
1.一种瓷砖胶，其特征在于，按重量份数计，包括以下原料：水泥30-40份、过-30目筛的无机多孔材料粉体55-65份和任选的助剂0.05-4份。2.根据权利要求1所述的瓷砖胶，其特征在于，按重量份数计，包括以下原料：水泥31-38份、无机多孔材料粉体56-63份和任选的助剂0.5-3.5份。3.根据权利要求2所述的瓷砖胶，其特征在于，按重量份数计，包括以下原料：水泥33-37份、无机多孔材料粉体58-62份和任选的助剂1-3份。4.根据权利要求1所述的瓷砖胶，其特征在于，无机多孔材料粉体的原料包括火山岩、轻质隔墙板废渣或发泡陶瓷保温板废渣中的一种或多种。5.根据权利要求1所述的瓷砖胶，其特征在于，所述水泥包括硅酸盐水泥、铝酸盐水泥、硫铝酸盐水泥中的一种或多种。6.根据权利要求1-5任一项所述的瓷砖胶，其特征在于，所述助剂包括保水增稠剂，粘合剂和可再分散乳胶粉；优选地，所述保水增稠剂0.1-0.3份，优选为0.12-0.28份，进一步优选为0.15-0.2...
【专利技术属性】