一种防水型泡沫混凝土配方及其制备方法组成比例
Waterproof foam concrete formula and preparation method thereof
The invention relates to a waterproof foam concrete formula and a preparation method. The formula comprises 60~70 parts of cement, 0~18 parts of fly ash, 1~2 parts of fiber, 5~10 parts of foaming agent, 0.5 to 2 parts of waterproof agent, 0.5 to 2 parts of admixture and 15~25 parts of water. The preparation methods include three steps: pulping, foaming and mixing. The waterproof foam concrete formula is added with water repellent, which has waterproof effect, makes it difficult to damp, ensures that the performance of thermal insulation can be brought into full play, and the waterproof foam concrete can achieve the strength by rationally mixing the proportion of cement and foaming agent and controlling the foaming time. And insulation requirements, but also to reduce the quality and improve the convenience of construction.
【技术实现步骤摘要】
一种防水型泡沫混凝土配方及其制备方法
本专利技术涉及一种建筑材料，特别是一种防水型泡沫混凝土配方及其制备方法。
技术介绍
近几年来，随着有机保温材料易开裂、耐久性差、易燃、且燃烧生成有毒气体等缺点日益彰显，导致其市场份额及使用量明显降低。作为理想的替代品，无机保温材料因其安全性高的突出优点而倍受青睐。采用无机保温材料制的泡沫混凝土，具有质量轻、保温隔热、吸音隔音、使用寿命长、无毒害等优点。现有技术方案：但普通泡沫混凝土制品在生产应用中仍然存在着如下几个方面的问题：①泡沫混凝土脆性较大，工程施工较困难（泡沫混凝土制品在运输、吊装、固定等施工过程中极易造成损坏）；②泡沫混凝土不能兼顾强度与保温隔热要求，密度等级越大，强度越高则保温隔热性能越差；③泡沫混凝土防水性较差，受潮吸水后其保温隔热效果会迅速减弱。
技术实现思路
本专利技术的一目的在于克服上述现有技术存在的不足，而提供一种环保、成分配比合理的防水型泡沫混凝土配方，通过该配方生产出来的防水型泡沫混凝土具有质量轻、保温隔热、吸音隔音、使用寿命长、无毒害、强度高、防水效果好等优点，能更好的应用于工业化建筑领域。本专利技术的...
【技术保护点】
1.一种防水型泡沫混凝土配方，其特征是，包括水泥60～70份、纤维1～2份、发泡剂5～10份、防水剂0.5～2份、外加剂0.5～2份和水15～25份。
【技术特征摘要】
1.一种防水型泡沫混凝土配方，其特征是，包括水泥60～70份、纤维1～2份、发泡剂5～10份、防水剂0.5～2份、外加剂0.5～2份和水15～25份。2.根据权利要求1所述防水型泡沫混凝土配方，其特征是，所述水泥包含普通水泥和快硬水泥，所述普通水泥占所述水泥总量的50%～80%。3.根据权利要求1所述防水型泡沫混凝土配方，其特征是，所述纤维为聚丙烯纤维。4.根据权利要求1所述防水型泡沫混凝土配方，其特征是，所述发泡剂为采用植物蛋白与动物蛋白混合的复合型蛋白发泡剂。5.根据权利要求1所述防水型泡沫混凝土配方，其特征是，所述防水剂为硅烷改性的高分子防水防潮干粉材料。6.根据权利要求1所述防水型泡沫混凝土配方，其特征是，所述外加剂包含减水、稳泡和增稠成分。7.根...