The invention discloses a method for turning soft aluminum parts threads, which comprises the following steps: selecting a strong viscosity coolant; selecting a thread blade with a large pitch of 1 level to replace a thread blade with a normal pitch; adopting a lateral feed mode, the blade is fed with a conodont angle smaller than the rear angle; and cutting parameters are the thread single-step cycle. Ring back knife consumption ap=0.05mm ~ 0.07mm, line speed Vc=55 ~ 60rpm. G76 multiple thread cutting cycle instruction is used to process threads. The diameter of the top diameter of the thread of the soft aluminum part is processed in the processing thread, leaving no allowance. By reasonably choosing cooling fluid, blade, programming method and cutting parameters, the invention optimizes the whole processing technology system for turning soft aluminum parts thread, effectively solves the problem of thread rotting of soft aluminum parts, and guarantees the product quality.
【技术实现步骤摘要】
一种车削加工软铝零件螺纹的方法
本专利技术涉及机械加工
，特别是车削加工螺纹的
技术介绍
车削加工螺纹时，理想状态下，前工序的螺纹顶径光杆尺寸留有0.1mm～0.2mm余量，采用标准全牙型螺纹加工，精加工螺纹时，如图1所示，螺纹刀片（见图2）两个切削刃a和b都会参与切削，它可以切削出包括牙顶在内的整个螺纹牙形，切削刃a保证螺纹牙型的正确，切削刃b保证螺纹齿顶的正确。但是，由于软铝（如LF21R/LF21等）的材料特性，延伸性好，抗塑性变形能力较差，且加工中温度过高，极易出现沾刀，在刀尖形成积屑瘤，造成如图3、图4所示的螺纹烂牙。
技术实现思路
为了解决上述问题，本专利技术提供一种解决软铝零件车削加工螺纹烂牙的方法，易于实现，且能保证工件的加工质量和尺寸精度，提高生产效率。本专利技术技术方案为：本专利技术一种车削加工软铝零件螺纹的方法，包括以下步骤：S1：选择冷却液：选用粘性较强的冷却液；S2：选择刀片：选用大1级螺距的螺纹刀片替代需正常加工螺距的螺纹刀片;S3：采用侧向进刀方式，刀片以小于后角的牙形角进给加工；S4：选择切削参数：螺纹单次循环背吃刀量a...
【技术保护点】
1.一种车削加工软铝零件螺纹的方法，其特征在于，包括以下步骤：S1：选择冷却液：选用粘性较强的冷却液；S2：选择刀片：选用大1级螺距的螺纹刀片替代需正常加工螺距的螺纹刀片;S3：采用侧向进刀方式，刀片以小于后角的牙形角进给加工；S4：选择切削参数：螺纹单次循环背吃刀量ap=0.05mm～0.07mm，线速度Vc=55～60rpm。
【技术特征摘要】
1.一种车削加工软铝零件螺纹的方法，其特征在于，包括以下步骤：S1：选择冷却液：选用粘性较强的冷却液；S2：选择刀片：选用大1级螺距的螺纹刀片替代需正常加工螺距的螺纹刀片;S3：采用侧向进刀方式，刀片以小于后角的牙形角进给加工；S4：选择切削参数：螺纹单次循环背吃刀量ap=0.05mm～0.07mm，线速度Vc=55～60rpm。2.根据权利要求1所述一种车削加工软铝零件螺纹的方...