The invention discloses a plastic processing method, the plastic processing steps are as follows: (1) adjusting the injection molding machine temperature to 200; Processing; (4) Cooling the polyethylene plastic processed from the injection molding machine; (5) Cutting the cooled polyethylene plastic into granular plastic, and packaging storage. After adding the flame retardant decabromodiphenyl ether in the polyethylene plastic, the plastic has good flame retardant performance, and the plastic mixture is easy to decompose after burning, and the generated gas does not pollute the air, thus having good environmental protection effect, and the plastic mixture has good thermal stability and can be used as a fuel. Long term preservation, give full play to flame retardant effect.
【技术实现步骤摘要】
一种塑料的加工方法
本专利技术涉及一种塑料的加工方法。
技术介绍
现代塑料通常是由石化产品源制备的。塑料通常由聚合物组成，包括重复分子单元的长链或单体。大部分塑料是由主链中仅仅含有碳的聚合物构成或主链中碳与氧、氮、氯或硫组合的聚合物形成。通过将不同的官能团引入到聚合物主链中或聚合物主链上，可以改变聚合物的性能。塑料的历史是随着天然材料(例如口香糖或虫胶)的发展而产生的。然而，这些材料需要特别昂贵和深入的方法来分离和处理天然产物。后来的发展包括使用化学改性的天然材料，例如橡胶和硝化纤维，再后来使用人造分子材料，例如环氧树脂、聚氯乙烯和聚乙烯。由于各种目的，包括包装、技术人造分子材料的发展导致塑料的使用在世界范围内增加。塑料是便宜并且容易制备的。
技术实现思路
针对现有技术的不足，本专利技术提供一种利用菜籽油油渣制备有机肥的方法，该方法充分利用油渣中的优质蛋白，并且提高油渣中各种养分的效率。为了实现上述目的，本专利技术通过以下技术方案实现：一种塑料的加工方法，所述该塑料加工步骤如下：(1)调节注塑机温度至200℃-350℃；所述的注塑机温度为250℃-300℃；(2)将聚乙烯塑料与阻燃剂放在一起进行搅拌混合；所述的阻燃剂为十溴二苯醚；所述的十溴二苯醚的熔点为285℃；(3)将混合好的塑料混合物放入注塑机中进行凝练加工；(4)把从注塑机中加工好的聚乙烯塑料进行冷却处理；(5)把冷却处理的聚乙烯塑切成粒状塑料，并打包存放。本专利技术的有益效果是：本专利技术在聚乙烯塑料中添加了阻燃剂十溴二苯醚后，能够使塑料具有很好的阻燃性能，而且该塑料混合物在燃烧后容易分解，并且产生的...
【技术保护点】
1.一种塑料的加工方法，其特征在于，所述该塑料加工步骤如下：(1)调节注塑机温度至200℃‑350℃；所述的注塑机温度为250℃‑300℃；(2)将聚乙烯塑料与阻燃剂放在一起进行搅拌混合；所述的阻燃剂为十溴二苯醚；所述的十溴二苯醚的熔点为285℃；(3)将混合好的塑料混合物放入注塑机中进行凝练加工；(4)把从注塑机中加工好的聚乙烯塑料进行冷却处理；(5)把冷却处理的聚乙烯塑切成粒状塑料，并打包存放。
【技术特征摘要】
1.一种塑料的加工方法，其特征在于，所述该塑料加工步骤如下：(1)调节注塑机温度至200℃-350℃；所述的注塑机温度为250℃-300℃；(2)将聚乙烯塑料与阻燃剂放在一起进行搅拌混合；所述的阻燃剂...