The invention provides a heat resistant adhesive tape and a manufacturing method thereof. The heat-resistant adhesive tape comprises a substrate layer and an adhesive layer arranged on the first surface of the substrate layer, and the substrate layer also includes a second surface opposite the first surface, the substrate layer being a glass fiber fabric impregnated with fluororesin, the surface roughness of the second surface being Rz < 2.5 micron or Ra < 1.0 micron. The heat-resisting adhesive tape of the invention has the characteristics of good smoothness, strong wear resistance, easy adhesion, not easy to break away from the adhesive body and high production efficiency due to adjusting the surface roughness of the non-adhesive surface of the adhesive tape.
【技术实现步骤摘要】
耐热性胶带及其制造方法
本专利技术涉及耐热性胶带，更具体而言涉及使用浸渗含氟树脂的玻璃纤维织物为基材的胶带。本专利技术还涉及上述胶带的制造方法。
技术介绍
己知使用浸渗有含氟树脂的玻璃纤维织物作为基材，并在该基材的一个面上设置有粘着剂层的胶带。该胶带显示出来自玻璃纤维织物及含氟树脂的高耐热性。玻璃纤维织物耐高温并且强度高，在耐高温胶带的制造时为了增加强度常将玻璃纤维织物用于基材的制造。特别是用在热封领域时，胶带张贴在热板上以后，由于胶带和被热封物接触，产生磨损。由于现有耐热性胶带的表面凹凸不平，导致使用时磨耗不平均，部分玻璃纤维容易裸露，使用寿命降低。另外，现有产品为了增加寿命而将基材氟树脂层加厚，此时张贴在具有角度的热板上的时候，导致弯曲后反发力大，所以不容易粘贴，容易脱离被粘体，导致胶带的使用寿命的降低。
技术实现思路
专利技术要解决的问题本专利技术的目的在于提供平整度好，耐磨性强，容易粘贴且不容易脱离被粘体，生产效率高的耐热性胶带及其制造方法。用于解决问题的方案本专利技术提供一种耐热性胶带，其包括基材层和在基材层的第一面上设置的粘着剂层，所述基材层还包括与所述第...
【技术保护点】
1.一种耐热性胶带，其包括基材层和在基材层的第一面上设置的粘着剂层，所述基材层还包括与所述第一面相对的第二面，所述基材层为浸渗含氟树脂的玻璃纤维织物，其特征在于，所述第二面的表面粗糙度为Rz≦2.5μm或Ra≦1.0μm。
【技术特征摘要】
1.一种耐热性胶带，其包括基材层和在基材层的第一面上设置的粘着剂层，所述基材层还包括与所述第一面相对的第二面，所述基材层为浸渗含氟树脂的玻璃纤维织物，其特征在于，所述第二面的表面粗糙度为Rz≦2.5μm或Ra≦1.0μm。2.根据权利要求1所述的耐热性胶带，其中所述基材层的所述第二面与所述玻璃纤维织物之间的最薄厚度为10～30μm。3.根据权利要求1或2所述的耐热性胶带，其中所述基材层的所述第二面与所述玻璃纤维织物之间的最薄厚度和所述基材层的所述第一面与所述玻璃纤维织物之间的最薄厚度的比例为0.8～1.3。4.根据权利要求1或2所述的耐热性胶带，其中所述含氟树脂为聚四氟乙烯(PTFE)、全氟烷氧基链烷烃(PFA)、全氟乙烯-丙烯共聚物(FEP)、乙烯-四氟乙烯共聚物(ETFE)、聚偏二氟乙烯(PVdF)中的一种或多种。5.根据权利要求1～4中任一项所述耐热性胶带的制造方法，其特征在于包括以下工序：使玻璃纤维织物进行含硅药剂处理...
【专利技术属性】
技术研发人员：李旭，渡边義宣，詹必才，
申请(专利权)人：日东电工上海松江有限公司，日东电工株式会社，
类型：发明
国别省市：上海,31