The invention discloses a thermal spraying sealing agent suitable for high temperature and high pressure underground environment and its application method. The preparation raw materials of the sealing agent are in mass fraction, including 60_70% polysiloxane, 5_10% filler and 25_30% sol. When used, the sealing agent is uniformly coated with the thermal spraying method. The coating surface is coated with a thickness of 10 20 micron, so that the pore sealing agent is fully penetrated into the pores of the coating, and then the pore sealing agent is dried at 60 80 The sealing agent provided by the invention has good permeability and stability, and has excellent corrosion resistance to H2S and CO2.
【技术实现步骤摘要】
一种适用于高温高压井下环境的热喷涂封孔剂及其使用方法
本专利技术属于热喷涂配套
，涉及一种封孔剂制备及其使用方法，具体涉及一种适用于高温高压井下环境的热喷涂封孔剂及其使用方法。
技术介绍
国内一些中低产气井含有H2S、CO2酸性气体，同时气井地层水中Cl-和矿化度较高，在H2S、CO2、Cl-综合作用下，碳钢管柱腐蚀严重，部分井3-5年即发生腐蚀穿孔。这类井由于单井产量低，选择高级耐蚀合金的话，单井管材成本大幅升高，影响油田开发效益，需寻求经济高效的防腐措施来提高管材的耐蚀性。热喷涂作为表面处理防腐工艺，可以在不改变在用金属管材力学性能的前提下，在金属管材表面形成防腐层，以较低的费用提高管材防腐性能，在国内外油田和海洋环境中广泛应用，取得了很好的防腐效果。但是热喷涂防腐层在喷涂材料熔融和冷却过程中，不可避免地有孔隙。孔隙会导致酸性腐蚀气体等渗入防腐层，降低防腐层附着力，甚至失效，因此，性能优异的封孔剂对于提高热喷涂防腐层防腐效果意义重大。针对热喷涂封孔剂，国内进行了很多研究，中国专利CN104789086A介绍了基于酚醛树脂和环氧树脂的耐高温热喷涂封孔剂及其...
【技术保护点】
1.一种适用于高温高压井下环境的热喷涂封孔剂，其特征在于，以质量分数计，其制备原料包括：60‑70％聚倍半硅氧烷，5‑10％填料以及25‑30％溶胶。
【技术特征摘要】
1.一种适用于高温高压井下环境的热喷涂封孔剂，其特征在于，以质量分数计，其制备原料包括：60-70％聚倍半硅氧烷，5-10％填料以及25-30％溶胶。2.根据权利要求1所述的一种适用于高温高压井下环境的热喷涂封孔剂，其特征在于，所述的聚倍半硅氧烷制备方法如下：将3-缩水甘油醚氧丙基三甲氧基硅烷与正硅酸乙酯按质量比(70-90)：(10-30)混合，加入去离子水，以HCl为催化剂，其中H2O、HCl与3-缩水甘油醚氧丙基三甲氧基硅烷的摩尔比为(1-3)：(0.0003-0.001)：1，在60-90℃的温度下充分搅拌反应10-60min，生成聚倍半硅氧烷。3.根据权利要求1所述的一种适用于高温高压井下环境的热喷涂封孔剂，其特征在于，所述的填料为粒径20-50nm的陶瓷粉。4.根据权利要求1所述的一种适用于高温高压井下环境的热喷涂封孔剂，其特征在于，所述的溶胶为粒径10-20nm的二氧化硅水溶胶。5.一种适用于高温高压井下环境的热喷涂封孔剂的使用方法，其特征在于，包括以下步骤：步骤一：以质量分数计，将60-70％聚倍半硅氧烷，5-10％填料以及25-30％溶...
【专利技术属性】
技术研发人员：李明星，李琼玮，朱方辉，周明明，张振云，刘伟，董晓焕，奚运涛，
申请(专利权)人：中国石油天然气股份有限公司，
类型：发明
国别省市：北京,11
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。