一种涂料新材料及其制备方法技术

本发明专利技术公开了一种涂料新材料及其制备方法。由如下重量份数的原料制成：糠醇树脂80‑200份，三级胺丙烯酸酯100‑220份，聚醋酸乙烯酯20‑30份，硅油20‑30份，石墨烯3‑8份，流平剂10‑20份，固化剂3‑8份，填料30‑80份。本发明专利技术的涂料新材料，具有自洁功能，抗腐蚀能力强，在极端环境如潮湿，酸碱等长期有效，产品的使用寿命长，在低温条件下保存时间长，不容易固化，在常温使用时，又很容易固化，节约喷涂时间。

A new coating material and its preparation method

The invention discloses a new coating material and a preparation method thereof. Made from the following weight parts of raw materials: Furfuryl alcohol resin 80 200, tertiary amine acrylate 100 220, polyvinyl acetate 20 30, silicone oil 20 30, graphene 3 8, leveling agent 10 20, curing agent 3 8, filler 30 80. The new coating material of the invention has self-cleaning function, strong corrosion resistance, long-term effectiveness in extreme environment such as humidity, acid and alkali, long service life of the product, long storage time under low temperature conditions, and is not easy to solidify. When used at normal temperature, it is easy to solidify and saves spraying time.

【技术实现步骤摘要】
一种涂料新材料及其制备方法
本专利技术属于新材料技术开发领域，具体涉及一种涂料新材料及其制备方法。
技术介绍
随着电子设备产品要求的集成度越来越高，其表面容易受到落尘或者自然腐蚀的影响。要求电子设备的表面具有自洁和防腐的功能，一般涂覆防腐涂料来解决这一问题。目前的防腐涂料自洁功能不强，且容易受到极端环境如湿气，酸碱等的腐蚀老化失去功效。专利201210191710.8公开了一种防腐涂料，按重量份包括下列原料：20-30份的氯醋树脂，10-20份的松香改性酚醛树脂，5-10份的氯化石蜡，2-8份的硅烷偶联剂，6-20份的乙二醇乙醚醋酸酯，5-15份的氨基树脂，2-10份的填料。该涂料剂耐盐水性强，防腐性，但是，其不能自洁。专利201410735861.4公开了一种防腐自洁涂料，由以下原料按照重量份数制得，四甲基二乙烯基二硅氧烷20-30份；甲基乙氧基硅油25-40份；羟基含氢硅油10-15份；对氯甲苯15-20份；乙二酸1-5份；环丙醇0.1-0.5份；催化剂0.3-0.7份。该防腐自洁涂料虽然能自洁，但是，涂料性能不佳，耐候性差，使用寿命短，容易受到极端环境的影响。
技术实现思路
本专利本文档来自技高网...

【技术保护点】
1.一种涂料新材料，其特征在于，由如下重量份数的原料制成：糠醇树脂80‑200份，三级胺丙烯酸酯100‑220份，聚醋酸乙烯酯20‑30份，硅油20‑30份，石墨烯3‑8份，流平剂10‑20份，固化剂3‑8份，填料30‑80份。

【技术特征摘要】
1.一种涂料新材料，其特征在于，由如下重量份数的原料制成：糠醇树脂80-200份，三级胺丙烯酸酯100-220份，聚醋酸乙烯酯20-30份，硅油20-30份，石墨烯3-8份，流平剂10-20份，固化剂3-8份，填料30-80份。2.根据权利要求1所述一种涂料新材料，其特征在于，所述流平剂为丙烯酸酯单体，二甲苯，甲苯，聚丙烯酸，丙撑亚胺，四乙氧基硅烷，磷酸三乙酯，2-氨基-6-氯苯并噻唑中的一种或一种以上。3.根据权利要求1所述一种涂料新材料，其特征在于，所述固化剂为碳酸钠，木质素磺酸钙，氯化钙，磺化丙酮的甲醛缩合物，山梨醇单月桂酸酯，1H,1H-全氟辛基胺，4-三氟甲硫基苯甲酸，3-乙...

【专利技术属性】
技术研发人员：周欢欢，
申请(专利权)人：天津安南科技有限公司，
类型：发明
国别省市：天津,12