一种新型耐火涂料制造技术

本发明专利技术涉及一种新型耐火涂料，将二苯醚甲醛树脂、二苯醚甲醛树脂、硼酸锌、氢氧化二铝、杀菌防腐剂、三氧化二锑、石墨纤维、原料按重量份组成。本发明专利技术的优点在于：本发明专利技术的新型耐火涂料，在原料中添加莫来石粉而能够在许多高温炉衬中使用，且各原料通过合理配比，使得涂料的热分解温度明显高于普通涂料，可大大增强涂料的耐火性能、热辐射及节能效果，也提高了其表面强度；同时，该涂料耐腐蚀、抗冲击力强、附着力强且不易脱落。

A new type of refractory coating

The invention relates to a new type of refractory coating, which consists of two phenyl ether formaldehyde resin, two phenyl ether formaldehyde resin, zinc borate, two aluminum hydroxide, bactericidal preservative, three oxidized two antimony, graphite fiber and raw materials. The invention has the advantages of novel fireproof coating of the invention, adding mullite powder can be used in many high temperature furnace lining in the raw material, and the raw material through the reasonable proportion of the coating thermal decomposition temperature was higher than that of ordinary paint, can greatly enhance the refractory coating, thermal radiation and energy saving effect, but also improve the surface strength; at the same time, the coating corrosion resistance, strong impact resistance, strong adhesion and not easy to fall off.

【技术实现步骤摘要】
一种新型耐火涂料
本专利技术涉及涂料
，特别涉及一种新型耐火涂料。
技术介绍
随着经济的发展，人类对涂料的需求量日益增大，并且在一些特定的地方需要特殊的涂料，如锅炉的内壁、内缸需要耐火材料。耐火温涂料是指在一定时限内，一定温度段内，能够经受高温环境氧化腐蚀的涂料，从而保护被涂物能在高温下正常工作，用于可燃性基材表面，用于提高被涂材料耐火极限的一种特种涂料，防火涂料涂覆在基材表面，除具有阻燃作用以外，还具有防锈、防水、防腐、耐磨和耐热性能，其涂层具有坚韧性、着色性、黏附性、易干性和一定的光泽，可广泛应用于钢铁制造、冶金、石油工业、天然气开采、航空航天等工业领域；目前虽已生产出多种耐火涂料仍满足不了需求，如何制备一种耐火性能优异，可满足窑炉耐火性能的涂料成为目前需要解决的技术问题。
技术实现思路
本专利技术要解决的技术问题是提供一种耐火性能优异，可满足窑炉耐火性能的新型耐火涂料。为解决上述技术问题，本专利技术的技术方案为：一种新型耐火涂料，其创新点在于：其原料按重量份包括如下组分：二苯醚甲醛树脂30份；硼酸锌25份；氢氧化二铝20份；杀菌防腐剂1份；三氧化二锑16份；石墨纤维6-份。本本文档来自技高网...

【技术保护点】
一种新型耐火涂料，其特征在于：其原料按重量份包括如下组分：二苯醚甲醛树脂 30份；硼酸锌25份；氢氧化二铝20份；杀菌防腐剂1份；三氧化二锑16份；石墨纤维6‑份。

【技术特征摘要】
1.一种新型耐火涂料，其特征在于：其原料按重量份包括如下组分：二苯醚甲醛树脂30份...