A heat-resistant exterior wall insulation coating and its preparation method are prepared by mixing organosilicon resin, dodecyl dicarboxylic acid, methacrylic acid, preservative, high chlorinated polyethylene resin, slag powder, aluminum hydroxide and propylene glycol methyl ether acetate. During the construction, the antiskid paint slurry is added with a curing agent for mixing. The coating is a thick paste type coating with good anti-skid, anti-corrosion and wear resistance. The coating is widely used in anti-skid and anti-corrosion of ladder climbing, roof of tank, ramp aisle, etc., playing a safe and protective role.
【技术实现步骤摘要】
一种耐高温外墙保温涂料及其制作方法
本专利技术属于涂料领域,特别涉及一种耐磨防滑的绝缘涂料。
技术介绍
涂层的主要作用是保护建筑物表面,使其具有防水、耐污、美观等特点,根据不同场合的需要,涂料还可以具有隔热、耐曝晒等功能,现有的耐高温复合外墙保温涂料在施工完成后由于附着性不佳,往往会出现开裂、剥落的情况,无法实现对建筑物外墙的保护,且不美观。
技术实现思路
本专利技术的目的是提供一种耐高温外墙保温涂料及其制作方法,本涂料涂层的防滑、防腐和耐磨性能好。采用的技术方案是:一种耐高温外墙保温涂料及其制作方法,是由有机硅树脂6-8kg、十二碳二羧酸0.5-1kg、甲基丙烯酸2-3kg、防腐剂1-2kg、高氯化聚乙烯树脂1-2kg、矿渣粉20-30kg、氢氧化铝0.5-1kg和丙二醇甲醚乙酸酯40-60kg混合制备而成。在施工时在所述的防滑漆浆加入固化剂10-20kg进行混合。施工时,将由有机硅树脂6-8kg、十二碳二羧酸0.5-1kg、甲基丙烯酸2-3kg、防腐剂1-2kg、高氯化聚乙烯树脂1-2kg、矿渣粉20-30kg、氢氧化铝0.5-1kg和丙二醇甲醚乙酸酯40-60kg混合制备而成的防滑漆浆内,加入固化剂10-20kg,进行混合后使用。混合后有效使用时间为8小时,实干24小时,被涂刷的设备投入使用的时间为7天。其优点在于:本涂料以化学防腐和物理防滑相结合,混合施工方便,涂层厚度可达3-5mm,为厚浆型涂料,具有良好的防滑、防腐并且耐磨性能。本涂料广泛应用于贮罐爬梯、罐顶、斜坡过道等的防滑防腐,起到安全保护作用。具体实施方式实施例一一种耐高温外墙保温涂料及其制作 ...
【技术保护点】
1.一种耐高温外墙保温涂料及其制作方法,其特征是由有机硅树脂6‑8kg、十二碳二羧酸0.5‑1kg、甲基丙烯酸2‑3kg、防腐剂1‑2kg、高氯化聚乙烯树脂1‑2kg、矿渣粉20‑30kg,、氢氧化铝0.5‑1kg和丙二醇甲醚乙酸酯40‑60kg混合制备而成;在施工时在所述的防滑漆浆加入型号为N‑75的固化剂10‑20kg进行混合。
【技术特征摘要】
1.一种耐高温外墙保温涂料及其制作方法,其特征是由有机硅树脂6-8kg、十二碳二羧酸0.5-1kg、甲基丙烯酸2-3kg、防腐剂1-2kg、高氯化聚乙烯树脂1-2kg、矿渣粉20-30kg,、氢氧化铝0.5-1kg和丙二醇甲醚乙酸酯40-60kg混合制备而成;在施工时在所述的防滑漆浆加入型号为N-75的固化剂10-20kg进行混合...