The invention discloses a non-sticky hand consumable material for 3D printing pen and a preparation method thereof. The raw material comprises oligomer, photoinitiator, co-initiator, anti-adhesive, thickener, light diffusive powder and paste/color powder. According to the weight percentage, the materials include oligomer 55%~90%, photoinitiator 3%~12%, co-initiator 1%~5%, anti-adhesive 1%~8%, thickener 1%~15%, photodiffusion powder 0.5%~2%, paste/toner residue. The cost of the 3D printing pen is 10% of the traditional non-stick consumables, the curing temperature should be within 45 C, the curing time should be within 8 seconds, the adhesive chirality is low before curing, the surface can be wiped off with paper towel, the cured surface is also dry, the viscosity coefficient is less than 50 cps, which is not achieved by the traditional similar products.
【技术实现步骤摘要】
一种3D打印笔用不粘手耗材及其制备方法
本专利技术属于3D打印机领域，尤其涉及一种3D打印笔用不粘手耗材及其制备方法。
技术介绍
3D打印笔技术是一种革命性的工业成型技术，相对于传统绘画而言，更加生动形象，增加儿童动手能力。原材料经过3D打印机便能直接成型，它是一种数字模型文件为基础，运用粉末状金属或塑料等可粘合材料，通过逐层打印的方式来构造物体的技术，不需经过模具的制造，节省了模具制造的时间及成本，随着3D打印技术的迅速发展，其对材料的要求也迅速提高。目前市场上的产品，大多数分为两种，一种是采用PCL材料的耗材，优点是使用温度低，安全低温，但是凝固时产品粘度大，凝固后表面不干爽，且产品韧性差易折断；另一种采用PLA材料的耗材，使用温度在180～230℃，温度过高易产生烫伤危险，并且由于使用温度高，使得使用本耗材的3D打印笔必须通电操作，当电源较远时就产生打印笔无法使用的情况。综上所述，如何专利技术一种使用温度低、固化速度快、固化产品干爽不粘手是亟待解决的问题。
技术实现思路
：本专利技术提出了一种3D打印笔用不粘手耗材及其制备方法，通过合理化配方，得到产品使用温度低...
【技术保护点】
1.一种3D打印笔用不粘手耗材，其特征在于，其材料按照重量百分比包括：聚物55%～90%、光引发剂3%～12%、助引发剂 1%～5%、抗粘剂1%～8%、增稠剂1%～15%、光扩散粉0.5%～2%、色膏/色粉余。
【技术特征摘要】
1.一种3D打印笔用不粘手耗材，其特征在于，其材料按照重量百分比包括：聚物55%～90%、光引发剂3%～12%、助引发剂1%～5%、抗粘剂1%～8%、增稠剂1%～15%、光扩散粉0.5%～2%、色膏/色粉余。2.如权利要求1-2任一项所述的一种3D打印笔用不黏手耗材，其特征在于，齐聚物可以为苯二甲酸乙二酯、聚氨酯丙烯酸树脂中的任意一种或多种的组合；光引发剂为2,4,6-三甲基苯甲酰基苯基膦酸乙酯；助引发剂为4-二甲基氨基苯甲酸乙酯；抗粘剂可以为棕榈酸乙基已酯、碳酸二辛酯中的一种或多种组合；增稠剂为椰油酸甲基单乙醇酰。3.如权利要求2任所述的一种3D打印笔用不黏手耗材，其特征在于，按重量百分比，2,4,6-三甲基苯甲酰基苯基膦酸乙酯的加入量为9.2～10.1%，更进一步优选为9.8。4.如权利要求2所述的一种3D打印笔用不黏手耗材，其特征在于，其原料按重量百分...