The invention discloses a high strength and high toughness aluminum alloy and a preparation method thereof. The aluminum alloy is melted from the following components and contents: Cu 1.3_2.3wt%, Zn 6.5_10.0wt%, Mg 2.2_2.9wt%, Zr 0.05_0.12wt%, Mn 0.4_0.8wt%, Ti 0.03_0.13wt%, Sr 0.089;0.11wt%, Ta 0.06_0.9;0.9wt%, Co. The.04 margin is 0.1wt% Al. The invention is based on the existing high-strength aluminum alloy elements, assisted by other elements, on the basis of improving the strength, the toughness of the aluminum alloy is still maintained at a higher level; on the basis of the formula, two-stage homogenization treatment and deformation strengthening are adopted, and the treatment steps are simplified.
【技术实现步骤摘要】
一种高强高韧铝合金及其制备方法
本专利技术属于金属材料领域，具体涉及一种用于力学性能优异的铝合金及其制备方法。
技术介绍
铝合金是以铝为基的合金的总称，主要合金元素包括铜、硅、镁、锌、锰，次要元素含有镍、铁、钛、锂等，具有密度低、比强度高、韧性好和耐腐蚀等优点，长期以来在航空航天领域广泛使用，而在材料的选用上，高强铝合金都占据着重要的地位，例如民用飞机上铝合金结构材料重量百分比达到70-80％。高强度铝合金主要是以Al-Zn-Mg-Cu系为主的合金，并开发出数十种铝合金牌号，但是上述牌号的铝合金强度为496-648MPa、伸长率5-13％，为了进一步提高该类铝合金的力学性能，技术人员在现有高强铝合金基础上开发了其它强度更高的合金，例如专利CN105543593A《高硬、高强、高韧性铝合金及其制备及同步器齿环的制法》公开的铝合金包括7.36-10.21％的Zn，2.18-3.56％的Mg，1.9-2.8％的Cu，0.15-0.40％的Zr，0.12-0.36％的Fe，0.05-0.45％的Si,0.01-0.03的Er/La/Ce。该铝合金的伸长率可以达到10.3％...
【技术保护点】
1.一种高强高韧铝合金，其特征在于由以下成分及含量熔炼而成：Cu 1.3‑2.3wt％、Zn 6.5‑10.0wt％、Mg 2.2‑2.9wt％、Zr 0.05‑0.12wt％、Mn 0.4‑0.8wt％、Ti 0.3‑1.3wt％、Sr 0.8‑1.1wt％、Ta 0.06‑0.20wt％、Co 0.4‑1.0wt％，余量为Al。
【技术特征摘要】
1.一种高强高韧铝合金，其特征在于由以下成分及含量熔炼而成：Cu1.3-2.3wt％、Zn6.5-10.0wt％、Mg2.2-2.9wt％、Zr0.05-0.12wt％、Mn0.4-0.8wt％、Ti0.3-1.3wt％、Sr0.8-1.1wt％、Ta0.06-0.20wt％、Co0.4-1.0wt％，余量为Al。2.根据权利要求1所述高强高韧铝合金，其特征在于由以下成分及含量熔炼而成：Cu1.6-2.0wt％、Zn7.5-9.0wt％、Mg2.4-2.7wt％、Zr0.07-0.09wt％、Mn0.5-0.6wt％、Ti0.6-0.95wt％、Sr0.9-1.0wt％、Ta0.10-0.16wt％、Co0.6-0.8wt％，余量为Al。3.根据权利要求1或2所述高强高韧铝合金，其特征在于，所述铝合金中杂质总含量≤0.01wt％。4.一种权利要求1-3任一项所述高强高韧铝合金的制备方法，其特征在于包括以下步骤(1)准备原料，(2)合金熔炼，(3)精炼处理，(4)均匀化处理，(5)挤压变形，(6)固溶处理，(7)时效处理；其中(1)准备原料：称取铝钛中间体、铝锰中间体、纯锌、阴极铜、纯镁，纯铝、铝锆中间合金、铝锶中间合金、纯钽、铝钴中间合金，上述金属及其合金中杂质总量控制在0.0...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。