本发明专利技术公开了钢结构防火涂料，通过将该防火涂料涂在钢材的表面，通过防火防火涂料对钢材起到保温和散热调节作用，提高钢结构的耐火极限，减少火灾损失，取得了显著效果，同时也具备较强的阻燃、耐腐蚀等特点，且生产成本低、工序简单且产品绿色环保，广泛适用于钢结构的建筑中。

A fire retardant coating for steel structure and its preparation method

The invention discloses a fire retardant coating for steel structure. By coating the fire retardant coating on the surface of steel, the fire retardant coating plays the role of heat preservation and heat dissipation regulation for steel, improves the fire resistance limit of steel structure, reduces fire losses, and achieves remarkable results. At the same time, the fire retardant and corrosion resistant coating has the characteristics of strong flame retardant and strong corrosion resistance. The production cost is low, the process is simple and the product is green and environmental friendly. It is widely used in steel structure construction.

【技术实现步骤摘要】
一种钢结构防火涂料及其制备方法
本专利技术涉及建筑材料
，尤其涉及一种钢结构防火涂料及其制备方法。
技术介绍
钢材是一种不会燃烧的建筑材料，它具有抗震，抗弯等特性。在实际应用中，钢材既可以相对增加建筑物的荷载能力，也可以满足建筑设计美感造型的需要；还避免了混凝土等建筑材料不能弯曲，拉伸的缺陷。因此钢材受到了建筑行业的青睐，单层，多层，摩天大楼，厂房，库房，候车室，候机厅等采用钢材都很普遍。但是，钢材作为建筑材料在防火方面又存在一些难以避免的缺陷，它的机械性能，如屈服点，抗拉及弹性模量等均会因温度的升高而急剧下降，钢结构通常在450～650℃温度中就会失去承载能力、发生很大的形变、导致钢柱、钢梁弯曲，结果因过大的形变而不能继续使用，一般不加保护的钢结构的耐火极限为15分钟左右，造成安全隐患。因此，钢材在使用时争强钢材的性能。
技术实现思路
本专利技术目的就是为了弥补已有技术的缺陷，提供钢结构防火涂料及其制备方法。本专利技术是通过以下技术方案实现的：钢结构防火涂料，由下述重量份的原料制得：粘结料8‐20，骨料15‐30，改性剂3-6、硬化剂2‐5，水30‐60。进一步的，所述粘结料为硅本文档来自技高网...

【技术保护点】
1.一种钢结构防火涂料，其特征在于，其是由下述重量份的原料制得：粘结料8‐20，骨料15‐30，改性剂3‑6、硬化剂2‐5，水30‐60。

【技术特征摘要】
1.一种钢结构防火涂料，其特征在于，其是由下述重量份的原料制得：粘结料8‐20，骨料15‐30，改性剂3-6、硬化剂2‐5，水30‐60。2.根据权利1所述的钢结构防火涂料，其特征在于，所述粘结料为硅酸盐水泥、氯氧化镁和膨润土中的一种或多种。3.根据权利1所述的钢结构防火涂料，其特征在于，所述骨料为膨胀蛭石、膨胀珍珠岩、硅酸铝纤维和矿棉中的一种或多种。4.根据权利1‐3任一所述的钢结构防火涂料的制备方法，其特征在于，包括以下步骤：(1)将粘结料、改性剂和硬化...

【专利技术属性】
技术研发人员：侯长华，
申请(专利权)人：佛山市三水万瑞达环保科技有限公司，
类型：发明
国别省市：广东,44