The invention discloses a two time cold rolling tin plate and a production method thereof, belonging to the technical field of rolling steel. According to the mass percentage, the chemical composition of the secondary cold-rolled tinplate is C:0.06%-0.09%, Si < 0.02%, Mn: 0.30%-0.50%, P < 0.015%, S < 0.012%, Als: 0.005%-0.02%, N: 0.0200%-0.0250%, Fe and the inevitable impurities. The production methods include continuous casting, hot rolling, pickling, cold rolling, continuous annealing, secondary cold rolling and tin plating. The invention can produce low cost, high strength and high plasticity tinplate through composition design and process optimization.
【技术实现步骤摘要】
一种二次冷轧镀锡板及其生产方法
本专利技术涉及轧钢
，特别涉及一种二次冷轧镀锡板及其生产方法。
技术介绍
二次冷轧镀锡板是在一次冷轧退火板的基础上进行二次冷轧后再通过连续电镀锡作业获得的在两面镀覆锡层的镀锡钢板或钢带。它具有强度高，厚度薄的特点，广泛应用于食品，饮料、化工等产品包装领域。当前国内外对二次冷轧镀锡板和二次冷轧镀锡原板均进行了大量的研究，取得了一些成果。如中国专利CN201410293390.6公开了一种罩退二次冷轧镀锡板的基板及其制造方法以及二次冷轧镀锡板，其成分为C0.02～0.06％，Si0.01～0.025％，Mn0.10-0.50％，Al0.06～0.12％，N0.001～0.003％，其余为Fe和杂质。该专利技术采用罩退工艺性能均匀性差，同时由于二次冷轧压下率高达20～50％，导致各向异性明显，塑性低。中国专利CN201110288961.3公开了一种高延伸的二次冷轧板及其制造方法，其成分为C0.15～0.20％，Si≤0.030％，Mn0.10-0.50％，P≤0.020％，S≤0.020％，Al0.01～0.05％，N0.0030...
【技术保护点】
1.一种二次冷轧镀锡板，其特征在于，按照质量百分比，所述镀锡板的化学成分为：C：0.06％～0.09％，Si≤0.02％，Mn：0.30％～0.50％，P≤0.015％，S≤0.012％，Als：0.005％～0.02％，N：0.0200％～0.0250％，余量为Fe及不可避免的杂质。
【技术特征摘要】
1.一种二次冷轧镀锡板，其特征在于，按照质量百分比，所述镀锡板的化学成分为：C：0.06％～0.09％，Si≤0.02％，Mn：0.30％～0.50％，P≤0.015％，S≤0.012％，Als：0.005％～0.02％，N：0.0200％～0.0250％，余量为Fe及不可避免的杂质。2.如权利要求1所述的二次冷轧镀锡板，其特征在于，所述二次冷轧镀锡板的内部显微组织为铁素体+渗碳体。3.如权利要求1所述的二次冷轧镀锡板，其特征在于，所述二次冷轧镀锡板的抗拉强度≥520MPa。4.如权利要求1所述的二次冷轧镀锡板，其特征在于，所述二次冷轧镀锡板的硬度HR30Tm≥71。5.如权利要求1所述的二次冷轧镀锡板，其特征在于，所述二次冷轧镀锡板的延伸率4％～14％。6.如权利要求1-5任一权利要求所...
【专利技术属性】
技术研发人员：方圆，吴志国，孙超凡，尹显东，莫志英，张召恩，朱防修，宋浩，王雅晴，石云光，崔阳，黄学启，周纪名，刘伟，张宝来，
申请(专利权)人：首钢集团有限公司，
类型：发明
国别省市：北京,11