The invention discloses a composite hydrogel, which is prepared by compounding currant gum, starch and sodium trimetaphosphate, sodium trimetaphosphate as crosslinking agent, starch as gel matrix, and currant gum as reinforcement compound into the hydrogel. The currant gum/starch composite hydrogel provided by the present invention has higher flexibility and hardness than the traditional sodium trimetaphosphate crosslinked starch hydrogel, is not easy to break down in water, and is quicker to form and has higher swelling property than the currant gum hydrogel crosslinked by sodium trimetaphosphate. It has broad application prospects.
【技术实现步骤摘要】
一种可得然胶/淀粉复合水凝胶及其制备方法和应用
本专利技术涉及一种复合水凝胶，特别是一种可得然胶/淀粉改性的复合水凝胶，属于化学复合材料领域。
技术介绍
可得然胶，又称热凝胶，凝结多糖，是由微生物发酵生产，以β-1,3-糖苷键构成的水不溶性葡聚糖，相对分子量约为50-200万。可得然胶属于天然生物分子，无毒无副作用，来源广泛。与众多天然多糖相比，具备开发的众多潜在优势：1)可得然胶生物降解性非常好，具有生物相容性及生物无毒性；2)在碱水中能够溶解，便于其进行均相化反应；3)其分子结构中含有多个活泼-OH，是结构修饰的理想位点，可通过化学改性提高可得然胶水溶性和化学活性。水凝胶是一种三维网状结构的含水材料，是一种在溶液中能够大量吸水而不溶解的物质。这些水凝胶一般都含有大量的亲水基团，并且其相互缠结的网状结构有助于水凝胶锁住其吸附的水分，帮助其在水中以较大比例地溶胀并在空气中持久的保持其含水结构。目前，水凝胶材料已被广泛应用于药物载体，创口敷料，生物组织修复，废水处理及农业储水等方面，根据所制备的水凝胶的强度和吸水性能的不同被用于不同的方向。如何制备成型快，溶胀度高，...
【技术保护点】
1.一种可得然胶/淀粉复合水凝胶，其特征在于由可得然胶、淀粉和三偏磷酸钠制备而成，可得然胶与玉米淀粉的质量比为1:1‑5，可得然胶、玉米淀粉的总质量与三偏磷酸钠的质量比为1:0.1‑1，可得然胶、玉米淀粉的总质量与水的质量比为1:10‑30。
【技术特征摘要】
1.一种可得然胶/淀粉复合水凝胶，其特征在于由可得然胶、淀粉和三偏磷酸钠制备而成，可得然胶与玉米淀粉的质量比为1:1-5，可得然胶、玉米淀粉的总质量与三偏磷酸钠的质量比为1:0.1-1，可得然胶、玉米淀粉的总质量与水的质量比为1:10-30。2.权利要求1所述的复合水凝胶，其特征在于所述可得然胶与玉米淀粉的质量比为1:2。3.权利要求1或2所述的复合水凝胶，其特征在于所述可得然胶、玉米淀粉的总质量与三偏磷酸钠的质量比为3:1。4.权利要求3所述的复合水凝胶，其特征在于所述可得然胶、淀粉和三偏磷酸的质量比为1:2:1。5.权利要求1所述复合水凝胶的制备方法，其特征在于包括如下步骤：(1)取一定量的可得然胶和玉米淀粉在0.1-5mol/LNaOH溶液中溶解，室温搅拌至固体溶解；(2)将步骤(1)所得到的溶液倒入烧杯...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。